1) the water-resisting property of the coating film
成膜耐水性能
1.
The relation of the Tg of emulsions and the water-resisting property of the coating film were build in this thesis.
在对广州金蝶涂料厂和美国联碳公司的苯－丙乳液进行对比分析的基础上，就合成乳液的玻璃化温度对 成膜耐水性能的影响进行了研究，找到了在一定的工艺条件下，苯－丙乳液的玻璃化温度与成膜耐水性能的关 系。
3) water fastness
耐水性能
1.
The effects of adding the cationic polymers poly-diallyl dimethyl ammonium chloride(PDMDAAC) and poly-diallyl dimethyl ammonium chloride-propylene acyl amine(PDMDAAC-AM) on the rate of ink absorption,the definition and water fastness of ink-jet recording materials have been studied.
研究了不同阳离子聚合物聚二甲基二烯丙基氯化铵(PDMDAAC)和二甲基二烯丙基氯化铵-丙烯酰胺共聚物(PDMDAAC-AM)对喷墨记录材料的吸墨速度、清晰度以及耐水性能的影响。
4) water resistance
耐水性能
1.
Study on Water Resistance of Polyurethane/Organic Montmorillonite Nano-composite;
聚氨酯/有机蒙脱土纳米复合材料耐水性能的研究
2.
Treating glass fibers surface with silane resin acceptor and styrene acrylic emulsion,which improved interfacial combine state of glass fibers gypsum composite effectively,and makes its mechanics properties and water resistance improve notably;Mix paraffin wax microemulsions,sulphate aluminium cement,etc.
采用硅烷偶联剂和苯丙乳液对玻璃纤维进行表面处理,有效地改善了玻璃纤维石膏复合材料的界面结合状况,使其力学性能和耐水性能得到显著提高;掺入石蜡乳液、硫铝酸盐水泥、聚乙烯醇等物质对石膏基体改性,各种外加剂相互作用,产生协同效应,提高了玻璃纤维/石膏复合材料的耐水性能;利用扫描电子显微镜对试样进行了微观分析,研究了外加剂改善复合材料耐水性能的作用机理。
3.
The effects of starch content in adhesive on bonding strength and water resistance were examined.
考察了小麦淀粉添加量对脲醛树脂胶应用于松木胶接时的胶合强度和耐水性能的影响。
5) water-resistance
耐水性能
1.
The effects of casting solvents on membrane compactness,crystallinity,water-resistance,and degradation in soil were investigated.
实验结果表明:铸膜液溶剂的挥发速度越慢,则膜的致密性越好,结晶度越高;醋酸酯淀粉膜在土壤中能降解,致密性好的膜耐水性能较好并且土壤降解速率较低。
2.
The results showed that mechanical property,heat-resistance property and water-resistance property of adhesive were improved significant.
采用AG-250KNI电子精密材料试验机和DTG-60H差热-热重分析仪对胶粘剂的力学性能和耐热性能进行了表征,采用常温水浸实验对胶粘剂的耐水性能进行了评价。
3.
The effects of fluorine monomer content on water-resistance of the emulsion films were studied through experiment of the water absorpti.
研究了不同乳化剂的配比对聚合稳定性和乳液的钙离子稳定性的影响,通过吸水率和接触角的测定研究了氟单体的用量对乳胶膜耐水性能的影响,并用透射电子显微镜(TEM)观察了乳胶粒子的形态。
补充资料：耐水性
分子式：
CAS号：
性质：漆膜耐水性是指漆膜对水作用的抵抗能力。常用的耐水性测量方法，分为常温浸水法、沸水浸泡法和加速耐水法等。常温浸水法是将涂漆样板的2/3面积浸泡在蒸馏水中，达到规定的时间后取出，检查漆膜是否有起泡、失光、变色、脱落等破坏现象。漆膜耐水性的好坏，直接影响到漆膜的使用寿命。它是涂料的一项重要质量指标。
CAS号：
性质：漆膜耐水性是指漆膜对水作用的抵抗能力。常用的耐水性测量方法，分为常温浸水法、沸水浸泡法和加速耐水法等。常温浸水法是将涂漆样板的2/3面积浸泡在蒸馏水中，达到规定的时间后取出，检查漆膜是否有起泡、失光、变色、脱落等破坏现象。漆膜耐水性的好坏，直接影响到漆膜的使用寿命。它是涂料的一项重要质量指标。