2) bursting strength decrease
顶破强力损失率
1.
The optimum conditions of neutral cellulose-enzyme treatment were decided through analyzing the value of weight loss,bursting strength decrease and bending rigidity of linen knitted fabrics.
为确定亚麻针织物中性纤维素酶的最佳处理工艺,以酶用量、温度、pH值和处理时间4个因素作为亚麻针织物酶处理因子,进行正交实验,并以织物的减量率、顶破强力损失率和织物抗弯刚度作为评价指标,最后确定出最佳工艺条件及参数。
3) loss in strength
强力损失
1.
1% to loss in strength,is a main process to affect strength.
初捻是影响强力损失的主要工序 ,占强力损失的 73 1 % ,初捻导丝钩是影响强力损失的主要部件 ,占初捻强力损失的 61 2 % ,气圈环和筒管的光洁度对强力损失也有一定的影
4) strength loss
强力损失
1.
For increasing the durability of durable press finished cotton fabrics, optimization of durable press finishing process, different swelling agents, fibrous strength protective agent R-CD, moisture curing process and highly active mixed catalyst system were investigated so as to improve strength loss without reduce crease recovery angles of treated cotton fabrics in this dissertation.
本研究拟通过对防皱整理工艺的优化、复合催化剂的应用、添加纤维保护剂以及潮态交联等途径来减少防皱整理织物的强力损失。
2.
The results showed that the whiteness increases by 50%-120%,yellowness decreases by 20%-40%,and shrinkage is less than 1% when the dry and wet burst strength loss is less than 5%.
结果表明,该体系可以使织物白度大幅提升50%~120%,黄度减少20%~40%,在干湿强力损失小于5%的情况下,缩水率小于1%。
5) strength loss ratio
强度损失率
6) deafness percent
听力损失率
补充资料：矿石损失率
矿石损失率
ore loss rate
kuongsh一sunshll.矿石损失率(ore 10、5 rate)损失工业储量与报销工业储量的百分比其计算式为 Q、一’ 5一六二只100% Q’\1一、·式中万为矿石损失率，丫;Q、为损失的工业储量，t:Q为报销的工业储量，t矿石损失率与矿石回采率的关系为 Q一Q、 万一一二~不二竺一1一}{、 Q式中Q、为采出的工业储最矿石损失率的功用与矿石回采率相同，其特点是从矿石损失方面反映矿产资源回采程度。为便于对矿石损失进行分析，对应崩矿与放矿将矿石损失分为一次矿石损失和_次矿石损失(见矿石损失与贫化)，并分别汁算一次(3’、)和二次(s2)矿石损失率。 Q、:、..，Q，_ 5，一万只“，‘，厂;‘一蓄’《‘〔，()一/S:、S:与总的矿石损失率(5)关系为 S一5]一5一5 152式中Q为上业储量.t:Q，为崩下的矿石最，t:Q、，、QS:分别为崩矿和放矿过程中损失的矿石量，t (刘兴国)