1) MA spinel
MA尖晶石
1.
The effect of added quantity of MA spinel powder and α-Al 2O 3 breeze on MgO based castable materials is studied.
主要研究了MA尖晶石粉和α-Al2O3微粉加入量对MgO质浇注料性能的影响。
2) MA spinel castable
MA尖晶石浇注料
1.
By using corundum,MgO powder,α-Al_2O_3 powder,calcium aluminate cement and SiO_2 powder as main starting materials,MA spinel castable is made in-situ reaction at high temperature.
以板状刚玉、镁砂、α-Al_2O_3微粉、纯铝酸钙水泥、SiO_2微粉为主要原料,通过高温下的原位尖晶石生成反应来制备MA尖晶石浇注料通过对基质中镁砂、SiO_2微粉、纯铝酸钙水泥等几项基质组分含量的调节,来研究各种组分对耐火浇注料性能的影响。
3) Spinel
[英][spi'nel] [美][spɪ'nɛl]
尖晶石
1.
Research progress of spinel-cobalt blue pigment;
尖晶石型钴蓝颜料的研究进展
2.
Preparation and Photocatalytic Performance of Spinel Type Composite Metal Oxides;
尖晶石型复合金属氧化物制备与光催化性能
3.
Studies on the Co-doping Modified Spinel LiMn_(1.98)Cr_(0.02)O_(4-y)Cl_y;
复合掺杂改性的尖晶石LiMn_(1.98)Cr_(0.02)O_(4-y)Cl_y的研究
4) NiFe2O4 spinel
NiFe2O4尖晶石
1.
In order to improve deficiencies of NiFe2O4 spinel used as matrix of inert anode in aluminium electrolysis.
为改善铝电解惰性阳极用NiFe2O4尖晶石材料存在的不足,制备了不同金属Ag含量的Ag-NiFe2O4金属陶瓷,利用扫描电子显微镜观察显微组织,由X射线衍射分析化学成分,研究了Ag-NiFe2O4试样的体积密度、热震性、导电率以及腐蚀速率,并与纯NiFe2O4尖晶石对比,分析了其性能差异的原因。
5) Spinel-CSi2N4
尖晶石CSi2N4
6) NiFe_2O_4 spinel
NiFe2O4尖晶石
1.
Investigates the effect of ball milling parameters on the particle size of powdered NiFe_2O_4 spinel.
研究了球磨参数对NiFe2O4尖晶石粉料的颗粒粒径的影响·通过计算确定了试验所需钢球尺寸,在此基础上,进行正交试验选择合适的参数·试验结果表明,球磨时间是影响粒径的主要因素,而研磨体级配对粒径分布范围有较大影响·确定合适的球磨参数为:球磨时间36h;研磨体级配35∶40∶25;料球比1∶2;球磨介质的体积分数为75%
补充资料：半透明烧结镁铝尖晶石陶瓷
分子式：
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。
CAS号：
性质：又称半透明烧结镁铝尖晶石陶瓷。在0.3～6.5μm范围的线性光透射率大于10％，可见光范围的总透射率约为75％。用镁-铝的盐或氢氧化物的热分解产物为原料，添加少量烧结促进剂氧化钙等。在真空中经1800～1900℃或湿氢气氛中1700℃左右烧结成半透明陶瓷。可用于制作高温电弧、密封外壳、天线窗、红外透射装置等。