挤出膨胀性能,die sw,音标,读音,翻译,英文例句,英语词典

您的位置：首页 -> 词典 -> 挤出膨胀性能

1) die sw 点击朗读

挤出膨胀性能

The microstructure,rheological properties and die swell of clay/SBR nano composite and carbon black/SBR compound were investigated with TEM and Monsanto rheometer.

用透射电子显微镜和孟山都流变仪研究了SBR粘土纳米复合材料和SBR炭黑混炼胶的微观结构、流变性能和挤出膨胀性能。

2) die swell 点击朗读

挤出膨胀

It was found that the die swell ratio (B) and the entrance pressure drop (ΔPENT) increased with increasing the diameter ratio (DR/D) of the reservoir to the die , and the relationship between ΔPENT and B wasbasically linear : B=B0 +KΔPENT, where the coefficients B0 and K were related to the experimental conditions , which characterized the el.

结果表明,试样的挤出膨胀比(B)和入口压力降(△P_(ENT))随着料筒与口型直径比的增加而增大,△P_(ENT)与B大致呈线性关系:B=B_0+K△P_(ENT),其中,待定系数B_0和K与实验条件有关。

The effects of surface tension and die swell on the shape of extrudate during micro profile extrusion were studied and compared both analytically and numerically.

分别用解析法和数值模拟法研究了聚合物微轮廓挤出成型过程中的在表面张力和挤出膨胀作用下挤出物的形变,并进行了比较,同时分析了表面张力和挤出膨胀共同作用下的形变。

3) extrusion swelling 点击朗读

挤出膨胀

This paper is formed by four parts:Firstly, the stress relaxation and extrusion swelling characteristics of several kinds of raw rubbers such as star SSBR, SSBR2305, ESBR1502 and BR9000 and their rubber carbon balck compounds have been studied.

本论文的研究分为四个部分:第一部分:研究了星形SSBR,SSBR2305,ESBR1502,BR9000纯胶及其炭黑混炼胶的应力松弛和挤出膨胀特性。

The relationship between stress relaxation and extrusion swelling of the compounds was investigated.

研究了4种胎面用胶[星形全偶联溶聚丁苯橡胶(S-SSBR)、偶联度为40%的SSBR 2305、乳聚丁苯橡胶(ESBR),顺丁橡胶(BR)]生胶及其混炼胶的应力弛豫特性,分析了弛豫机理,考察了混炼胶的应力弛豫和挤出膨胀性能间的关系。

4) die swell 点击朗读

挤出膨胀率

5) expansion property 点击朗读

膨胀性能

Study of the expansion property of API L80 casing; 点击朗读

APIL80套管的膨胀性能试验研究

Carbide formation law of Fe-38Ni-Mo-V-C series alloy has been studied with physical methods of magnetic and expansion property testing.

采用磁性能和膨胀性能测试的物理方法,研究了Fe-38Ni-Mo-V-C系合金的碳化物形成规律。

更多例句>>

6) thermal expansion property 点击朗读

热膨胀性能

The thermal expansion property testing indicated that the CTEs of the composites were increased non-linearly with the temperature; When SiC volume fraction was a certain, the CTEs of the composite decreased with the SiC particle si.

以电子封装基片为应用背景,采用挤压铸造方法制备了体积分数为55%,不同颗粒粒径增强的SiCp/Cu复合材料,并分析测试了颗粒粒径和热处理状态对材料热膨胀性能的影响规律。

The AH36 and Q345 steels were chosen for their measurement of thermal expansion property, and the change law for thermal expansion property of cast slab between the processes of heating and cooling at different temperature change rate was studied.

选取AH36,Q345两个钢种进行热膨胀性能测试,研究了连铸坯在升降温过程和不同升降温速度条件下热膨胀性能的变化规律。

更多例句>>

补充资料：不锈钢的物理性能、力学性能和耐热性能

不锈钢的物理性能

不锈钢和碳钢的物理性能数据对比，碳钢的密度略高于铁素体和马氏体型不锈钢，而略低于奥氏体型不锈钢；电阻率按碳钢、铁素体型、马氏体型和奥氏体型不锈钢排序递增；线膨胀系数大小的排序也类似，奥氏体型不锈钢最高而碳钢最小；碳钢、铁素体型和马氏体型不锈钢有磁性，奥氏体型不锈钢无磁性，但其冷加工硬化生成成氏体相变时将会产生磁性，可用热处理方法来消除这种马氏体组织而恢复其无磁性。

奥氏体型不锈钢与碳钢相比，具有下列特点：

1）高的电阴率，约为碳钢的5倍。

2）大的线膨胀系数，比碳钢大40％，并随着温度的升高，线膨胀系数的数值也相应地提高。

3）低的热导率，约为碳钢的1/3。

不锈钢的力学性

不论不锈钢板还是耐热钢板，奥氏体型的钢板的综合性能最好，既有足够的强度，又有极好的塑性同时硬度也不高，这也是它们被广泛采用的原因之一。奥氏体型不锈钢同绝大多数的其它金属材料相似，其抗拉强度、屈服强度和硬度，随着温度的降低而提高；塑性则随着温度降低而减小。其抗拉强度在温度15~80°C范围内增长是较为均匀的。更重要的是：随着温度的降低，其冲击韧度减少缓慢，并不存在脆性转变温度。所以不锈钢在低温时能保持足够的塑性和韧性。

不锈钢的耐热性能

耐热性能是指高温下，既有抗氧化或耐气体介质腐蚀的性能即热稳定性，同时在高温时双有足够的强度即热强性。

不锈钢国际标准标准

标准标准名

GB 中华人民共和国国家标准（国家技术监督局）

KS 韩国工业标准协会规格Korean Standard

AISI 美国钢铁协会规格America Iron and Steel Institute

SAE 美国汽车技术者协会规格Society of Automative Engineers

ASTM 美国材料试验协会规格American Society for Testing and Material

AWS 美国焊接协会规格American Welding Society

ASME 美国机械技术者协会规格American Society of Mechanical Engineers

BS 英国标准规格British Standard

DIN 德国标准规格Deutsch Industria Normen

CAS 加拿大标准规格Canadian Standard Associatoin

API 美国石油协会规格American Petroleum Association

KR 韩国船舶协会规格Korean Resister of Shipping

NK 日本省事协会规格Hihon Kanji Koki

LR 英国船舶协会规格Llouds Register of Shipping

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

膨胀性能影响早期微膨胀性能吸水膨胀性能土壤膨胀性能吸湿膨胀性能挤出膨化

膨胀性能<冶> 挤出性能挤后膨胀挤压膨化性能高性能膨胀剂

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 挤出膨胀性能 1) die sw 挤出膨胀性能 1. The microstructure,rheological properties and die swell of clay/SBR nano composite and carbon black/SBR compound were investigated with TEM and Monsanto rheometer. 用透射电子显微镜和孟山都流变仪研究了SBR粘土纳米复合材料和SBR炭黑混炼胶的微观结构、流变性能和挤出膨胀性能。 2) die swell 挤出膨胀 1. It was found that the die swell ratio (B) and the entrance pressure drop (ΔPENT) increased with increasing the diameter ratio (DR/D) of the reservoir to the die , and the relationship between ΔPENT and B wasbasically linear : B=B0 +KΔPENT, where the coefficients B0 and K were related to the experimental conditions , which characterized the el. 结果表明,试样的挤出膨胀比(B)和入口压力降(△P_(ENT))随着料筒与口型直径比的增加而增大,△P_(ENT)与B大致呈线性关系:B=B_0+K△P_(ENT),其中,待定系数B_0和K与实验条件有关。 2. The effects of surface tension and die swell on the shape of extrudate during micro profile extrusion were studied and compared both analytically and numerically. 分别用解析法和数值模拟法研究了聚合物微轮廓挤出成型过程中的在表面张力和挤出膨胀作用下挤出物的形变,并进行了比较,同时分析了表面张力和挤出膨胀共同作用下的形变。 3) extrusion swelling 挤出膨胀 1. This paper is formed by four parts:Firstly, the stress relaxation and extrusion swelling characteristics of several kinds of raw rubbers such as star SSBR, SSBR2305, ESBR1502 and BR9000 and their rubber carbon balck compounds have been studied. 本论文的研究分为四个部分:第一部分:研究了星形SSBR,SSBR2305,ESBR1502,BR9000纯胶及其炭黑混炼胶的应力松弛和挤出膨胀特性。 2. The relationship between stress relaxation and extrusion swelling of the compounds was investigated. 研究了4种胎面用胶[星形全偶联溶聚丁苯橡胶(S-SSBR)、偶联度为40%的SSBR 2305、乳聚丁苯橡胶(ESBR),顺丁橡胶(BR)]生胶及其混炼胶的应力弛豫特性,分析了弛豫机理,考察了混炼胶的应力弛豫和挤出膨胀性能间的关系。 4) die swell 挤出膨胀率 5) expansion property 膨胀性能 1. Study of the expansion property of API L80 casing; APIL80套管的膨胀性能试验研究 2. Carbide formation law of Fe-38Ni-Mo-V-C series alloy has been studied with physical methods of magnetic and expansion property testing. 采用磁性能和膨胀性能测试的物理方法,研究了Fe-38Ni-Mo-V-C系合金的碳化物形成规律。更多例句>> 6) thermal expansion property 热膨胀性能 1. The thermal expansion property testing indicated that the CTEs of the composites were increased non-linearly with the temperature; When SiC volume fraction was a certain, the CTEs of the composite decreased with the SiC particle si. 以电子封装基片为应用背景,采用挤压铸造方法制备了体积分数为55%,不同颗粒粒径增强的SiCp/Cu复合材料,并分析测试了颗粒粒径和热处理状态对材料热膨胀性能的影响规律。 2. The AH36 and Q345 steels were chosen for their measurement of thermal expansion property, and the change law for thermal expansion property of cast slab between the processes of heating and cooling at different temperature change rate was studied. 选取AH36,Q345两个钢种进行热膨胀性能测试,研究了连铸坯在升降温过程和不同升降温速度条件下热膨胀性能的变化规律。更多例句>> 补充资料：不锈钢的物理性能、力学性能和耐热性能不锈钢的物理性能不锈钢和碳钢的物理性能数据对比，碳钢的密度略高于铁素体和马氏体型不锈钢，而略低于奥氏体型不锈钢；电阻率按碳钢、铁素体型、马氏体型和奥氏体型不锈钢排序递增；线膨胀系数大小的排序也类似，奥氏体型不锈钢最高而碳钢最小；碳钢、铁素体型和马氏体型不锈钢有磁性，奥氏体型不锈钢无磁性，但其冷加工硬化生成成氏体相变时将会产生磁性，可用热处理方法来消除这种马氏体组织而恢复其无磁性。奥氏体型不锈钢与碳钢相比，具有下列特点： 1）高的电阴率，约为碳钢的5倍。 2）大的线膨胀系数，比碳钢大40％，并随着温度的升高，线膨胀系数的数值也相应地提高。 3）低的热导率，约为碳钢的1/3。不锈钢的力学性不论不锈钢板还是耐热钢板，奥氏体型的钢板的综合性能最好，既有足够的强度，又有极好的塑性同时硬度也不高，这也是它们被广泛采用的原因之一。奥氏体型不锈钢同绝大多数的其它金属材料相似，其抗拉强度、屈服强度和硬度，随着温度的降低而提高；塑性则随着温度降低而减小。其抗拉强度在温度15~80°C范围内增长是较为均匀的。更重要的是：随着温度的降低，其冲击韧度减少缓慢，并不存在脆性转变温度。所以不锈钢在低温时能保持足够的塑性和韧性。不锈钢的耐热性能耐热性能是指高温下，既有抗氧化或耐气体介质腐蚀的性能即热稳定性，同时在高温时双有足够的强度即热强性。不锈钢国际标准标准标准标准名 GB 中华人民共和国国家标准（国家技术监督局） KS 韩国工业标准协会规格Korean Standard AISI 美国钢铁协会规格America Iron and Steel Institute SAE 美国汽车技术者协会规格Society of Automative Engineers ASTM 美国材料试验协会规格American Society for Testing and Material AWS 美国焊接协会规格American Welding Society ASME 美国机械技术者协会规格American Society of Mechanical Engineers BS 英国标准规格British Standard DIN 德国标准规格Deutsch Industria Normen CAS 加拿大标准规格Canadian Standard Associatoin API 美国石油协会规格American Petroleum Association KR 韩国船舶协会规格Korean Resister of Shipping NK 日本省事协会规格Hihon Kanji Koki LR 英国船舶协会规格Llouds Register of Shipping 说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条膨胀性能影响早期微膨胀性能吸水膨胀性能土壤膨胀性能吸湿膨胀性能挤出膨化