1) quenching cyclic spheroidized annealing
淬火-循环球化退火
2) cycling spheroidal annealing
循环球化退火
1.
The results show that the microstructure and properties of the die steel after cycling spheroidal annealing,1110 ℃quenching and 520 ℃ twice tempering are optimal.
讨论了热处理工艺对铸造新型高合金冷作模具钢组织与性能的影响,结果表明,采用循环球化退火及1110℃淬火520℃两次回火得到的性能最佳,回火组织为回火马氏体及残余奥氏体,其硬度可达57～60HRC,冲击韧度8～10J/cm2。
3) circular quenching
循环淬火
1.
40CrNiMo steel had been investigated through circular quenching.
坯料制备是半固态成形技术中的一个关键问题,以40CrN iMo钢为研究对象,提出了循环淬火法制备半固态坯料的方法。
4) cycling quenching
循环淬火
1.
Through the analyses of hardness and microstructures of the heat-treated materials,the optimum treatment process was determined,which was the treatment of cycling quenching at 860 ℃ three times.
针对日前国内瓦楞辊工作寿命远远低于国外水平的现状,从瓦楞辊的材质与热处理工艺入手,根据热处理后硬度和显微组织分析,确定在860℃3次循环淬火为最佳的处理工艺,既可提高机体强度又可提高其韧性,从而使瓦楞辊的耐磨性和疲劳强度得到提高。
5) Accelerated Cyclic Spheroidizing annealing
快速循环球化退火
6) spheroidal annealing
球化退火
1.
Production of spheroidal annealing of cold rolled 25 steel strip;
25钢冷轧球化退火钢带的生产
2.
To introduce a new process for making needle latch steel wire with diameter range 0 34～0 53mm The technological process consists of patenting-phosphating-cold drawing-spheroidal annealing under Ac 1 point in electrical heating furnace-slight drawing to finished product The theoretical basis and advantages of the main points of new process are emphatically elaborate
该工艺流程是：铅淬火—磷化—拔丝—Ａｃｌ以下电加热连续退火炉球化退火—轻拉至成品。
补充资料：球化退火
分子式：
分子量：
CAS号：
性质：将钢加热到稍低于或稍高于共析钢或过共析钢的温度，然后缓冷下来。目的在于使珠光体内的片状渗碳体以及先共析渗碳体都变为球粒状，均匀分布于铁素体基体中（这种组织称为球化珠光体）。具有这种组织的中碳钢和高碳钢硬度低）。具有它种组织的中碳钢和高碳钢硬度低，被切削性好，冷形变能力大。对工具钢来说，这种组织是淬火前最好的原始组织。
分子量：
CAS号：
性质：将钢加热到稍低于或稍高于共析钢或过共析钢的温度，然后缓冷下来。目的在于使珠光体内的片状渗碳体以及先共析渗碳体都变为球粒状，均匀分布于铁素体基体中（这种组织称为球化珠光体）。具有这种组织的中碳钢和高碳钢硬度低）。具有它种组织的中碳钢和高碳钢硬度低，被切削性好，冷形变能力大。对工具钢来说，这种组织是淬火前最好的原始组织。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。