1) basie castable
碱性浇注料
1.
The weakness of magnesia - alumina basie castable is the poor slag penetration resistance.
氧化镁-氧化铝碱性浇注料一个弱点为抗渗透性差,为改善钢包浇注料抗渣性能,提高其使用效果和寿命,运用静态坩埚法研究含AlON的MgO-Al_2O_3浇注料抗渣性。
2) Alkali resistant castable refractory
耐碱浇注料
1.
Alkali resistant castable refractory was produced using hard clay clinker as main raw material and adding in potash feldspar, ceramic powder etc.
以焦宝石熟料为主要原料,添加钾长石、瓷粉等外加物,制备了耐碱浇注料。
3) high performance alkali resistant castables
优质耐碱浇注料
4) Castables
浇注料
1.
The effects of the grain size of fused corundum and amounts of magnesia,cement and silica micropowder as additives on the behavior of linear expansion of the corundum-spinel castables in sintering process were studied.
在750~1450℃的温度下测量了试样的线膨胀率,研究了电熔刚玉粒度、氧化镁、水泥及硅微粉加入量对刚玉-尖晶石质浇注料烧成过程中线膨胀率的影响。
2.
CO resistance of sol-gel bonded castables was studied together with the CO resistance of cement bonded castables.
研究了新型溶胶-凝胶结合耐火浇注料的抗CO侵蚀性能,同时也与传统的水泥结合耐火浇注料进行了对比试验,并从侵蚀前后的表观特征、理化性能和微观结构等多方面探讨了其CO侵蚀作用机理。
3.
Based on the Problems of heat shack rupturing and desquamating of firebricks on trolley of heat treatment furnaces,the technology measures were put forward irrigating trolley liner using castables with high resisting heat shack performance.
针对台车式热处理炉台车衬砖热震断裂脱落问题,提出了采用高抗热震性浇注料进行台车工作衬整体浇注的技术措施,根据热处理炉的实际工作条件,完成了浇注料的研制,并在实际应用中,取得了良好的应用效果。
5) castable refractory
浇注料
1.
The application of the castable refractory in the carbon kiln lining and the way of improving lining service life;
浇注料在炭素回转窑内衬施工中的应用及提高内衬使用寿命的途径
2.
Effect of Heat Treatment Temperature on Properties of Calcined Flint Clay-Bauxite Castable Refractory
热处理温度对焦宝石-铝矾土浇注料性能的影响
3.
The characteristic of castable refractory was advanced by analyzing the service conditions on Water-cooled Beam of heating furnace in this paper.
通过对加热炉水冷梁使用条件的分析,提出了该类浇注料应具有的特点。
6) casting material
浇注料
1.
Research and application of the casting material reinforced by steel fibre;
钢纤维增强浇注料的研究与应用
2.
The synthesis of low relative molecular weight of poly(acrylate sodium)and application of them as dispersant on bauxite-based low-cement casting material were studied.
研究了低相对分子质量的聚丙烯酸钠合成及其作为分散剂在矾土基低水泥浇注料上的应用。
3.
The experience of successful application of new early-strengthening high-aluminium casting material to 650 rolling mill continuous oil combusting pusher-type heating furnace is described in this paper.
阐述了新型早强高铝质浇注料在６５０轧机燃油推钢连续式加热炉上应用的经验。
补充资料：不锈钢纤维增强耐火浇注料
不锈钢纤维增强耐火浇注料
stainless steel fibers reinforced castable refractories
韧性和抗震性能明显提高。 根据不锈钢纤维含铬、镍等元素不同，钢纤维分为“502”、“310”、“330”等不同的牌号。金属铬含量增加可提高钢纤维的抗氧化性能，金属镍含量增加可提高钢纤维的高温韧性和机械强度。不同品种的不锈钢纤维对耐火浇注料性能的影响见图。不锈钢纤维增强耐火浇注料的技术性能见表。 7厂-一一-----一-------------一--一门 荟12{ 娜、’}了/.} 豁}”一} 车{。~、、~一一} 侣_}‘、—尹/沪) 鸳，…_!月卜卜汁‘一叮{ 川}、l‘只、n 加热温工之r 不同品种的不锈钢纤维对耐火浇注料 加热后抗折强度的影响 1一不加钢纤维.2一加入302钢纤维.3一加入310钢纤维; 4一加入330钢纤维钢纤维对耐火浇注料技术性能的影响止 应用不锈钢纤维增强耐火浇注料已大量应用于轧钢加热炉炉底水管包扎、加热炉炉辊(见彩图插页第19页)、均热炉炉盖衬、锻造炉内衬、出铁沟沟盖衬、出钢槽衬等部位，使用寿命比普通耐火砖或耐火烧浅料高2一5倍，具有显著经济技术效果。 (张炳根)buxiugangx旧nwe!zengqiang naihuo Jiaozhuliao不锈钢纤维增强耐火浇注料(stainless steelfibers reinforeed eastable refraetories)以铝酸盐水泥作为结合剂，与耐火骨料、粉料、外加剂和不锈钢纤维配制的可浇注耐火材料。(见衬火浇注抖)钢纤维含量为0.6%~2.5%。这种浇注料具有高温下整体性好、耐磨性和抗热震性强等特点，适用于高温下有机械震动、热冲击、磨损等特殊部位。按其选用的骨料材质可分为粘土质、高铝质、硅质、镁质等多种不锈钢纤维增强耐火浇注料。 性能一般炉体内衬在使用时均存在高、中、低3个温度区域，如用耐火浇注料筑造炉衬，则往往在低温区与高温区之间形成一个强度薄弱区，不锈钢纤维在这个区域起着显著的增强作用，将炉衬内外连成一体，延迟了炉衬的开裂，即使开裂后也可以紧紧地把裂缝两侧的炉衬拉紧而不致过早地脱落。不锈钢纤维对炉衬高温工作区也有增强作用，主要是提高了浇注料的韧性、抗机械冲击性能和抗热震性，因此可以提高炉衬整体使用寿命。随着钢纤维含量的增加，耐火浇注料的
说明：补充资料仅用于学习参考，请勿用于其它任何用途。