1) titania-silica
氧化钛-氧化硅
2) Titanium-containing silica
含钛氧化硅
4) alumina/titania/silica
氧化铝/氧化钛/氧化硅
5) TiO2-SiO2 composite oxide
钛硅复合氧化物
1.
The TiO2 and TiO2-SiO2 composite oxide were prepared by Sol-gel method and characterized by XRD,BET and DRS.
用溶胶-凝胶法制备了TiO2和钛硅复合氧化物,对样品进行了X射线衍射(XRD)、比表面积测试(BET)和紫外-可见漫反射光谱(DRS)分析,并以甲基橙为模拟污染物,考察了其光催化性能。
2.
Preparative methods of sol-gel,hydrolysis precipitation,hydrothermal synthesis for photocatalysts of TiO2-SiO2 composite oxide at home and abroad are introduced in this paper.
介绍了溶胶–凝胶法、水解沉淀法、水热合成法制备钛硅复合氧化物光催化剂的研究进展,评述了3种制备方法的优缺点以及添加硅对TiO2光催化活性的影响:添加硅后增大了催化剂的比表面积,提高了TiO2晶型转变温度,增强了其表面酸度,生成的Ti—O—Si键抑制了TiO2粒径的增大,拓宽了催化剂的禁带宽度,从而提高了光催化剂的催化活性。
6) titanium-silica mixed oxides
钛硅混合氧化物
1.
Three-Dimentionally Ordered macroporous titanium-silica mixed oxides were successfully synthesized by using polystyren sphere colloid crystal as the template and the sol of tetraethyl silicate and tetrabutoxy-titane as the filling fluid.
以聚苯乙烯微球离心后形成的三维规则排列的胶晶作模板,用钛酸丁酯和正硅酸乙酯分别和水、乙醇等配制成的混合溶胶填充微球之间的间隙,然后原位形成凝胶,最后通过焙烧(<5℃/min;300℃,5h;570℃,5～10h,空气流速1L/min)除去微球得到三维规则排列的大孔钛硅混合氧化物。
补充资料：一氧化钛
分子式： TiO
CAS号：
性质：金黄色粉末。含氧52％～54％(原子)。体心立方结构。密度4.888g/cm3。熔点1750℃。可溶于40％(质量)氟氢酸中。易为热的浓硫酸、浓盐酸和浓硝酸侵蚀。也可为浓碱侵蚀。与30％(质量)过氧化氢作用生成黄色溶液。为强还原剂。在空气加热时，于150～200℃转变为三氧化二钛。真空中1600℃加热金属钛和二氧化钛混合物、2000℃下氢还原二氧化钛或1000℃下镁还原二氧化钛，均可得到一氧化钛。一氧化钛具有氧或钛缺位性质，可用作电子材料。
CAS号：
性质：金黄色粉末。含氧52％～54％(原子)。体心立方结构。密度4.888g/cm3。熔点1750℃。可溶于40％(质量)氟氢酸中。易为热的浓硫酸、浓盐酸和浓硝酸侵蚀。也可为浓碱侵蚀。与30％(质量)过氧化氢作用生成黄色溶液。为强还原剂。在空气加热时，于150～200℃转变为三氧化二钛。真空中1600℃加热金属钛和二氧化钛混合物、2000℃下氢还原二氧化钛或1000℃下镁还原二氧化钛，均可得到一氧化钛。一氧化钛具有氧或钛缺位性质，可用作电子材料。