1) soft interface layer
弱界面层
2) weak-boundary layer theory
弱界面层理论
3) weak boundary layers
弱界层
4) weak interface
弱界面
1.
Research progress in machanible ceramics with weak interfaces in microstructure and materials design;
可加工陶瓷的弱界面结构特征及其研究进展
2.
The failure process and mechanism of a brittle composite matrix,reinforced with long fibers with weak interface,is studied.
研究了弱界面长纤维增强脆性基复合材料在单轴拉伸荷载下的力学性能及其破裂机理和破坏过程。
3.
The special stepped and multi-layered fracture of CePO_4, toge-(ther) with the network structure of intercalated distributional strong-weak interface forming with the addition of CePO_4 which can yield and capture micro-defect, dissipate energy of primary c.
针对工程陶瓷材料本征脆性问题,作者从应力 应变曲线、压痕及压痕尖端的裂纹扩展等方面探讨了可加工Ce ZrO2/CePO4材料的"塑性化",并从显微结构入手,研究了使这种材料产生"塑性化"的机理,即除CePO4本身具有一定的台阶和层片状断裂外,主要由于CePO4的引入出现了强弱界面共同存在的网络结构,弱界面可以产生和捕获微观缺陷,耗散主裂纹扩展能量,导致局部的剪切变形,从而赋予陶瓷"塑性"。
6) weak boundary
薄弱界面
1.
The results showed that the yield strength of composite depended on the shear strength at the weak boundary,which was determined by the boundary adhesion and the length,diameter and content of short fibre.
结果发现 ,屈服强度由薄弱界面的剪切强度决定 ,而界面的剪切强度则取决于界面粘合、短纤维长度、直径以及含量等因素 ;拉伸过程中复合材料的界面按照剪切强度由小到大的顺序分段依次被破坏直至断裂 ;短纤维含量较低时 ,其拉伸强度主要由短纤维拔出后的基体承担 ,同时受应力集中影响很大 ,短纤维含量较高时断裂强度则更接近于屈服强度。
补充资料：弱界面层理论
分子式：
CAS号：
性质：该理论由Bikerman提出，认为当被粘物、胶黏剂及环境中的低分子物或杂质，通过渗析、吸附及聚集过程，在部分或全部界面内产生，这些低分子物富集区，就是弱界面层。当受外力作用时，破坏过程必然发生在弱界面层。
CAS号：
性质：该理论由Bikerman提出，认为当被粘物、胶黏剂及环境中的低分子物或杂质，通过渗析、吸附及聚集过程，在部分或全部界面内产生，这些低分子物富集区，就是弱界面层。当受外力作用时，破坏过程必然发生在弱界面层。