1) Thermal dewmposition mechanism
裂解阻燃机理
2) flame-retardant mechanism
阻燃机理
1.
The flame-retardant mechanism of EVA/APP/EG system has been investigated by TGA,SEM,FTIR and XPS.
对聚磷酸铵(APP)和膨胀石墨(EG)协同阻燃乙烯-醋酸乙烯酯共聚物(EVA)及其阻燃机理进行了研究。
2.
Then, the flame-retardant mechanism of the intumescent flame-retardant PU coatings was investigated by TGA, SEM, FTIR and ELA.
用自制的新型成炭剂和聚磷酸铵复配作为聚氨酯防火涂料的阻燃体系,采用热失重分析、扫描电镜、红外光谱和元素分析等手段对膨胀型聚氨酯防火涂料的阻燃机理进行了较为深入的研究。
3.
The thesis discourses flame-retardant mechanism of polyester and introduces various type of flame-retardant agent,narrates the current situation of flame-retardant polyester as well as analysing the developing trend of flame-retardant agent of polyester.
论述了阻燃涤纶纤维的阻燃机理,介绍了各种类型的阻燃剂,说明了阻燃涤纶纤维的当前发展情况,并对今后阻燃涤纶纤维阻燃剂研制方向进行了展望。
3) flame retardant mechanism
阻燃机理
1.
The flame retardant mechanism of BCPPO was described in detail and the characteristic of each synthetic technics was commented objectively by analyzing the synthetic technics of different scholars.
笔者详细阐述了BCPPO的阻燃机理,通过分析不同研究者制备BCPPO的合成工艺,客观评述了各种工艺的特点,并全面介绍了BCPPO在高分子材料领域的应用,对今后BCPPO的研究提出了一些建议。
2.
In addition, flame retardant mechanism of microcapsules flame retardent are also introduced;lastly,the further development of the new materials are prospected.
介绍了微胶囊阻燃剂的阻燃机理,并对微胶囊阻燃材料的发展作了展望。
3.
The flame retardant mechanism of BCPPO was described and the characteristic of each synthetic technics was commented objectively by analyzing the synthetic technics of different scholars.
阐述了BCPPO的阻燃机理;通过分析不同研究者制备BCPPO的合成工艺,客观评述了各种工艺的特点;并全面介绍了BCPPO在高分子材料领域中的应用;对今后BCPPO的研究提出了一些建议。
4) flame retarding mechanism
阻燃机理
1.
Study on the formation of the carbonaceous layer of flame retarding coating and its flame retarding mechanism;
防火涂料炭质层形成及阻燃机理的研究
2.
The flame retarding mechanism of polyazodiphenylene phenylphosphonate (PAPPP) to PET was investigated by thermogravimetry (TGA) and pyrolysis gas chromatography-mass spectroscopy (PGC-MS).
300,与纯PET相比,共混物的热解温度范围变宽,残余量增加,且在PET燃点附近的可燃性挥发气体的生成量降低,表现为凝聚相阻燃机理。
3.
The samples′ DTA curves were measured and the flame retarding mechanism was studied.
通过比较阻燃整理前后试样的差热分析曲线,对阻燃机理进行了初步探讨。
5) fire retardant mechanism
阻燃机理
1.
This paper summarize the fire retardant mechanism of thermo-plastical plastic, the fire retardant agents in common use and their fire retardant effect in detail.
综述了热塑性塑料的阻燃机理、常用阻燃剂及其阻燃作用，指出无毒、无污染、低价格是塑料阻燃抗静电技术的发展方向。
2.
Advanced instruments and analyzing methods such as DTA, TG, SEM, XRD, FTIR are used to study the fire retardant mechanism of the expanding fire coating.
本文概述了防火涂料的发展，介绍了膨胀型防火涂料的组成，并采用先进的仪器和分析方法如差热分析法（ＤＴＡ），热重量分析法（ＴＧ）、电子扫描电子显微镜（ＳＥＭ）、Ｘ射线衍射（ＸＲＤ）、傅里叶变换红外光谱（ＦＴＩＲ）对膨胀型防火涂料的阻燃机理进行了探讨。
6) retardant mechanism
阻燃机理
1.
The retardant mechanism of Al(OH)3 was introduced in this paper.
介绍了氢氧化铝的阻燃机理、氢氧化铝表面改性和协同增效等改性方法,概述了氢氧化铝及其复合体系在塑料、橡胶、纤维等聚合物中的应用现状。
2.
Theory of plastic flame and retardant mechanism of halogenated flame - retardants are introduced in this paper.
本文阐述了塑料燃烧的理论和卤系阻燃剂的阻燃机理,并推断卤系阻燃剂与聚合物的热降解数据曲线可应用在指导阻燃材料的配方设计上,同时指出卤系阻燃剂依然有较好的发展前景。
3.
The combustion and fire- retardant mechanism of viscose fiber was introduced.
介绍了粘胶纤维的燃烧和阻燃机理,使用的阻燃剂、阻燃加工技术,以及国内外阻燃粘胶纤维的研究现状和主要产品。
补充资料：用氢氧化镁作阻燃剂制备阻燃PP的方法
聚丙烯（PP）以其密度小、力学性能好、耐化学腐蚀、易加工、耐热变形温度高、价格低廉等突出优点，在许多行业得到了广泛的应用。阻燃PP已成为使用阻燃剂量最大、增长最快的高聚物阻燃材料。氢氧化镁［Mg(OH)2］作为一种无卤阻燃剂，除能阻燃外还有消烟性能，而且脱水温度高，比较适于加工温度较高的PP等高聚物阻燃改性，在降低对环境的危害和材料安全处理方面更能满足有关法规的要求，同时也使阻燃塑料更易于再生利用。特别是Mg(OH)2原料来源丰富，价格低廉，用它作为PP的阻燃剂有较高的经济效益，所以近年全国各地对用Mg(OH)2阻燃PP十分重视。 然而目前多数企业在用Mg(OH)2阻燃PP时，由于Mg(OH)2用量不足，需添加其他阻燃剂，致使配方成本居高不下。为此，笔者谈一下在用Mg(OH)2作PP阻燃剂时应注意的一些事项。用Mg(OH)2阻燃PP时，为使材料达到ＵＬ94Ｖ-０阻燃级（3.2ｍｍ试样），用量应≥60%，不过，如用Mg(OH)2抑烟，则用量可低一些，含40%Mg(OH)2的PP的烟密度仅为未阻燃PP的约1/3。当PP中Mg(OH)2含量达65时，其机械性能，特别是抗冲强度和伸长率均显著劣化。为了使Mg(OH)2阻燃PP材料的力学性能不至下降很多，应选择粒径微细、粒径分布窄而均匀的Mg(OH)2作原料，并进行双偶联表面处理，以改善物料的流变性能，促进混炼加工时通过Mg(OH)2／PP表面导热而避免形成局部热点，并提高Mg(OH)2与PP的相容性，使其能在聚合物中较均匀地分散。 采用这种经处理的Mg(OH)2阻燃PP时，在对PP作增韧改性后，即使高Mg(OH)2含量的阻燃PP也可获得良好的加工性能及物理机械性能。为使Mg(OH)2在PP中均匀分散，可用布斯捏合机（ＢｕｓｓＫｅｎａｄｅｒ），或德国产双螺杆混炼挤出机，或往复式单螺杆混炼挤出机来进行混炼，并采用合理的加料混合混炼方式。例如，可将全部PP及增韧剂与所需量60%的Mg(OH)2第一次加入混合混炼机中先混合混炼数分钟后，再第二次加入余下的Mg(OH)2。 在加料时应注意加料要均匀，计量要准确。若采用密炼机混炼，对Mg(OH)2除采用两次加入法外，还要准确计量装料率在87%～93%范围内较好。当装料率较少时，混炼效果差，当装料率＞95%时，易造成Mg(OH)2凝集结团，难以分散均匀。混炼不均匀不仅使阻燃性能降低，而且拉伸强度和断裂伸长率都降低，制品外观也较差。总之，采用对PP良好的增韧改性，用经特殊表面处理并对粒径及粒度分布控制的Mg(OH)2，采用适宜的混炼机械及两次加料方法，可使Mg(OH)2在PP中分散均匀。这种阻燃PP可兼具很多应用领域所需材料的机械性能及阻燃性能，还具有抑烟、低毒、无卤、不用Ｓｂ2Ｏ３，环境友好，配方成本低的特点，有较高的经济效益和社会效益。