1) thermal shock resistance
热震性
1.
A new testing method--center heating technique has been employed for quantitatively studying the thermal shock resistance of CaO refractory.
用中心加热法研究了 ＣａＯ耐火材料的抗热震性能。
2.
The influence of additive SiO 2 with different content on the thermal shock resistance of plasma-sprayed Al 2O 3 coating was investigated.
通过在Ａｌ２Ｏ３陶瓷粉末中添加不同数量的ＳｉＯ２，探讨其对等离子喷涂涂层抗热震性的影响。
2) thermal shock resistance
抗热震性
1.
Thermal shock resistance of nano BN-SiC composites;
纳米BN复合SiC材料的抗热震性研究
2.
Effect of ZrO_2-SiC composite powder addition on thermal shock resistance of Al_2O_3-C refractories;
添加ZrO_2-SiC复合粉体对Al_2O_3-C质耐火材料抗热震性能的影响
3.
Research on preparation technology and thermal shock resistance of Al_2O_3/cordierite ceramics;
Al_2O_3/堇青石陶瓷的制备和抗热震性能研究
3) thermal shock resistance
热震性能
1.
The thermal shock resistance was evaluated.
为了研究纳米热障涂层的热震性能,采用等离子喷涂工艺制备了纳米Y2O3-ZrO2(YSZ)热障涂层,并测试了涂层的热震性能。
2.
In order to study the thermal shock resistance and thermal shock failure mechanism of Al_2O_3-TiO_2/NiCoCrAlY coatings,the samples were heated to 400℃ and hold a certain time then cooled to room temperature by quenching.
在 ZL104铝合金基体上喷涂了 Al_2O_3-TiO_2/NiCoCrAlY 系梯度涂层和 Al_2O_3-TiO_2非梯度涂层,对这两种试样进行了室温400℃冷热循环试验,以研究涂层的抗热震性能和热震失效机制。
3.
The microhardness, bonding strength and thermal shock resistance were tested.
运用扫描电镜对涂层显微结构进行观察和分析,同时测试了涂层的显微硬度、结合强度和热震性能。
4) Resistance to thermal shock
抗热震性
1.
The study shows that the resistances to thermal shock and to slag corrosion of the β-Sialon/SiC are better than β-Sialon/corundum, the fracture times of the resistance to thermal shock are up to 40.
结果表明:β-Sialon/SiC的抗热震性、抗渣侵蚀性优于β-Sialon/刚玉,在1100℃时,抗热震断裂次数达到40次以上。
2.
the characters of sic and the appliance are introduced,the influence on the resistance to thermal shock of kiln furniture is studied through experiments.
本文介绍了碳化硅的特点及其在窑具中的应用 ,通过试验探讨了其对窑具抗热震性的影
5) thermal shock failure
热震性能
1.
The results show that the coatings containing TiB2/Al2O3 and Cr3C2 exhibit favorable porosity, adherence, wear resistance and good resistance to thermal shock failure, in general, superior to those of Al2O3/ TiO.
涂层常规性能测试结果表明:含TiB2/Al2O3和Cr3C2 的涂层的孔隙率较低、结合强度高、具有优良的耐磨性及抗热震性能。
6) thermal shock
抗热震性
1.
The result shows that the coating,having high emissivity,bonds well with substrate and have better property of thermal shock resistance than Al2O3-SiC ceramic coating.
结果表明,该涂层有很高的发射率,与基材结合良好,抗热震性能明显优于Al2O3-SiC陶瓷涂层。
2.
The influences of RE2(CO3)3 content on the sintering temperatures,thermal shock,the bulk density on the solution and the phase comp.
以碳化硅、高岭土、氧化铝粉为原料,以质量分数为3%的混合碳酸稀土为助熔剂,烧制具有气孔率高、容重小、强度高、抗热震性高的莫来石-碳化硅质泡沫陶瓷过滤器。