1) brazing alloys for electronics and vacuum devices
电真空钎料
2) vacuum brazing / active brazer
真空钎焊/活性钎料
3) vacuum electron beam brazing (VEBB)
真空电子束钎焊
1.
During vacuum electron beam brazing (VEBB) of stainless steel with BNi-2 filler metal and manganese-base filler metal, the effects of VEBB processing parameters on wettability of filler metals and temperature field of workpieces are discussed.
探讨了在BNi -2钎料和锰基 7#合金两种钎料的不锈钢真空电子束钎焊过程中 ,真空电子束钎焊工艺参数对钎料润湿性和试板温度场的影响作用。
4) vacuum brazing
真空钎焊
1.
The craft and application of vacuum brazing for honeycomb material;
蜂窝材料的真空钎焊工艺及应用
2.
Influence of active element Mg on joint properties of aluminum alloy vacuum brazing;
活性元素镁对铝合金真空钎焊接头性能的影响
3.
Morphology of carbide on diamond interface by vacuum brazing;
真空钎焊金刚石界面碳化物的形貌
5) vacuum electron beam self-material brazing
真空电子束自钎焊
1.
Because the property of niobium alloy is far from that of stainless steel, some special welding techniques have been applied, such as explosive welding, vacuum braze welding, electric resistance welding, vacuum electron beam self-material brazing and so on.
因为二者的性能差别较大，所以通常采用一些特殊的方法进行焊接，如爆炸焊、真空钎焊、电阻焊和真空电子束自钎焊等。
6) low vacuum brazing
低真空钎焊
1.
A diamond composite material using a new Cu-32Mn-8Ti prealloyed powder as the adhesion matrix is fabricated in a low vacuum brazing environment.
采用自制Cu-32Mn-8Ti预合金粉末为粘合剂,在低真空钎焊条件下制备了金刚石复合材料。
补充资料：钎料
分子式：
CAS号：
性质：为实现两种材料（或零件）的结合，在其间隙内或间隙旁所加的填充物。钎料的熔点必须比焊接的材料熔点低。适宜于连接精密、复杂、多铤缝和异类材料的焊接。钎料按熔点高低分为软钎料（熔点低于450℃的钎料），硬钎料（熔点高于450℃的钎料）。钎料按组成分软钎料有锡基、铅基、锌基等钎料。硬钎料有铝基、银基、铜基、镍基等钎料。
CAS号：
性质：为实现两种材料（或零件）的结合，在其间隙内或间隙旁所加的填充物。钎料的熔点必须比焊接的材料熔点低。适宜于连接精密、复杂、多铤缝和异类材料的焊接。钎料按熔点高低分为软钎料（熔点低于450℃的钎料），硬钎料（熔点高于450℃的钎料）。钎料按组成分软钎料有锡基、铅基、锌基等钎料。硬钎料有铝基、银基、铜基、镍基等钎料。