3) Structural defect
组织缺陷
1.
The common structural defects in butt rammer made from WC-Co cemented carbides were listed and the evaluating principle and method for material quality of WC-Co alloy were exposed.
列举了人造金刚石生产专用WC－Co硬质合金顶锤材料中的常见组织缺陷，论述了硬质合金材质的评估原理和方法。
4) Structure defect
组织缺陷
1.
The influence of structure defect on the mechanical property of seamless steel tube;
无缝钢管组织缺陷及对力学性能的影响
2.
The results showed that there existed serious banded structure segregation in metallographic structure of valve disc,theδferrite distributed by chain at crystal boundary,structure defects greatly increased brittleness of valve disc materials.
结果表明:阀碟材料的显微组织中有较严重的带状组织偏析,同时δ铁素体在晶界上呈链状分布,这类组织缺陷大大增加了阀碟材料的脆性,在冲击载荷作用下导致了脆性断裂。
5) microstructure defect
组织缺陷
1.
The results show that microstructure defects, elbow thickness thinning of tube and insufficient steam quantity cause the bursting.
结果表明,水冷壁管存在的组织缺陷、弯曲处管壁较薄及蒸汽量不足是造成其开裂的主要原因,并提出了相应的预防措施。
2.
Microstructure defects, uneven hot rooling, elbow thickness thinning of tube also affected tube bursting.
另外 ,水冷壁管存在的组织缺陷、轧制不均匀以及弯曲处壁厚减薄也是造成水冷壁管爆裂不可忽略的因素。