1) copper-nickel slag
铜镍废渣
1.
The industrial copper sulfate was prepared from copper-nickel slag and the nickel in the slag was recorered by one-step leaching method with compressive oxiding.
采用湿法加压氧化一步浸取工艺处理铜镍废渣生产工业硫酸铜 ,并回收其中镍 ,试验结果表明 :铜镍总回收率达到 98 6 3% ,硫酸铜产品达到国标优等品 ,终渣形成氧化铁红产
2) Nickel-bearing copper slag
含镍铜渣
3) waste nickel slag
废镍渣
1.
Under the leaching conditions of w(H_2SO_4)25%,acid leaching time 3h,n(waste nickel slag) ∶n(H_2SO_4) of 1.
研究了以废镍铝合金粉(废镍渣)为原料、H2SO4为浸出剂、尿素为沉淀剂制备镍催化剂的方法;考察了N i浸出条件对其浸出率的影响,并通过催化加氢实验对镍催化剂的活性进行了评价。
4) Waste Residue Containing Nickel
镍废渣
1.
Study on Electrolytic Retrieving Metallic Nickel from Waste Residue Containing Nickel;
从含镍废渣中电解回收金属镍的研究
5) copper and nickel wastewater
铜镍废水
1.
Study on Fenton oxidation-coagulation process for treatment of complexing copper and nickel wastewater;
Fenton氧化-混凝联合工艺处理络合铜镍废水的研究
6) dregs containing copper
含铜废渣
1.
The basic cupric sulfate is prepared via ammonia treatment of dregs containing copper,catalytic oxidization,distillation and crystallization.
以含铜废渣为原料，采用氨浸、催化氧化、蒸馏、结晶的工艺制备碱式硫酸铜，探讨了氨浸机理，在正交试验的基础上得出了氨浸工艺条件，并对蒸氨等过程进行了研究。
补充资料：钯铜镍锰合金
分子式：
CAS号：
性质：是钯含铜、镍和锰的四元高温钎料合金，有PdCuNiMn55-15-10和PdCuNiMn35-20-15。前者的熔点1060～1105℃，钎焊温度1110℃。用真空感应炉形成牢固氧化膜的铝基、铬基、钛基合金以及抗蠕变的镍钼合金和钨、钼等材料。此合金抗剪强度较高，可在550～850℃的温度下工作，在原子能工业中得到应用。
CAS号：
性质：是钯含铜、镍和锰的四元高温钎料合金，有PdCuNiMn55-15-10和PdCuNiMn35-20-15。前者的熔点1060～1105℃，钎焊温度1110℃。用真空感应炉形成牢固氧化膜的铝基、铬基、钛基合金以及抗蠕变的镍钼合金和钨、钼等材料。此合金抗剪强度较高，可在550～850℃的温度下工作，在原子能工业中得到应用。