1) B 4C powders
B4C粉末
2) boron carbide
B4C
1.
High-temperature adhesive was prepared using phenol-formaldehyde resin (PF) as matrix and boron carbide (B_4C) as modifier.
以酚醛树脂为基体,加入B4C作为改性填料制备出高温粘结剂,并对Si3N4陶瓷进行粘接。
2.
This paper theoretically analyzes the wettability of boron carbide by liquid aluminum and discusses the wettability difference between theoretical and practical results based on the characteristics of aluminum and its interaction with boron carbide.
依据金属Al的特性及其与B4C相互作用的关系,在理论上分析Al对 B4C的润湿性,分析理论润湿性与实际润湿性差异的原因,在此基础上,通过实验寻求改善Al对B4C润湿性的方法和工艺,发现升高温度可以改善润湿性,温度由 1 050℃升至1 100℃时,润湿角θ由52°降至23°;在Al中添加小量Mg后,真空 1×10-3Pa,温度1 100℃×3 h时Al对B4C润湿角由原来的23°降至9°。
3.
A boron carbide-aluminum composite was produced by vacuum-pressure infiltration process.
采用真空—压力熔渗工艺制备了B4C/Al金属陶瓷复合材料。
3) powder
[英]['paʊdə(r)] [美]['paudɚ]
粉末
1.
Microstructural characteristic of rapidly solidified W9 high speed steel powders;
气体雾化快凝W9高速钢粉末的组织特征
2.
Selective laser sintering——A kind of rapid prototyping technology based on special powders;
特种粉末选择性激光烧结快速成形技术
3.
Status of Preparation and Application of Fe-Ni Alloy Powder;
铁镍合金粉末的制备及应用现状
4) powders
[英]['paudə] [美]['paʊdɚ]
粉末
1.
Hydrothermal treatment of barium strontium titanate (BST) powders obtained by solution-precipitation method;
溶胶-沉淀法制备钛酸锶钡粉末及其水热处理
2.
The Influence of Feed Way on Ferrite Powders Made by Hydrothermal Process;
加料方式对水热法制铁氧体粉末的影响
3.
Studies on hydroxyapatite powders via sol-gel process;
溶胶-凝胶法制备羟基磷灰石粉末的研究
5) pulverized powder
粉碎粉末
6) powder
[英]['paʊdə(r)] [美]['paudɚ]
粉，粉末;火药
补充资料：X射线粉末衍射法
分子式：
CAS号：
性质：在X射线衍射分析中，采用单色X射线和粉末状多晶样品进行衍射的一种方法。多晶试样大多数情况是多晶粉末，也可以是多晶片或丝。衍射线条的位置、强度，可用德拜法、聚焦法或针孔法等照相记录。粉末法主要用于物质鉴定、晶体点阵常数、多晶体的结构、晶粒大小、高聚物结晶度测定等。
CAS号：
性质：在X射线衍射分析中，采用单色X射线和粉末状多晶样品进行衍射的一种方法。多晶试样大多数情况是多晶粉末，也可以是多晶片或丝。衍射线条的位置、强度，可用德拜法、聚焦法或针孔法等照相记录。粉末法主要用于物质鉴定、晶体点阵常数、多晶体的结构、晶粒大小、高聚物结晶度测定等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条