1) A/S
铝硅比
1.
A concentrate with A/S over 7～12 can be obtained by the new process of elective crashing and grinding from bauxite with middle-low grade.
我国铝土矿绝大部分属于高铝、高硅一水硬铝石型矿石 ,铝硅比以 4～ 7为主 ,不宜直接采用拜耳法生产氧化铝。
2.
China is rich in bauxite resources, but our resources is diaspore with low ratio of A/S.
我国铝土矿属高铝、高硅的一水硬铝石型铝土矿，资源丰富，但铝硅比低，氧化铝溶出性能差，碱耗、能耗高，生产成本高。
3.
The results show that the more the hydro calcium ferrite is,the lower the A/S and N/S of the red mud is.
在添加水化铁酸钙的条件下系统进行了溶出中低品位铝土矿试验,结果表明,随水化铁酸钙添加量增多,溶出赤泥铝硅比、钠硅比降低;随配矿量减少、溶出温度升高、溶出时间延长,溶出赤泥铝硅比降低。
2) Low ratio of Al2O3/SiO2
低铝硅比
3) Low alumina-silicon ratio
低铝硅比生料
4) alumium and silicon ratio of crude material slurry
生料浆铝硅比
5) bauxite with low A/S
低铝硅比铝土矿
6) Al-Si Alloy
铝硅合金
1.
Modification mechanism of eutectic silicon in Al-Si alloys:impurity-induced coupled twinning;
铝硅合金中共晶硅的变质机理:杂质诱发共生成对孪晶
2.
Mechanism of Acid Pickling for Al-Si Alloy before Spiral Vibration Polishing;
铝硅合金螺旋振动抛光酸洗机理的探讨
3.
Effects of strong magnetic field on modification of Al-Si alloy;
强磁场对铝硅合金变质效果的影响
参考词条
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。