1) flame retardant graft polymer polyether polyol
难燃接枝聚合物聚醚多元醇
1.
The flame retardant flexible polyurethane foams (FPUF)was prepared from TDI and the mixture of new flame retardant graft polymer polyether polyols(FRGPPP) and polyether polyols 3050 by free foaming method.
用新型难燃接枝聚合物聚醚多元醇和聚醚多元醇3050的混合物与甲苯二异氰酸酯(TDI)自由发泡反应,制备了阻燃型聚氨酯软质泡沫。
2) polymer polyether polyol
接枝聚合物聚醚多元醇
3) graft polyether polyol
接枝聚醚多元醇
5) flame retardant polyether polyol
阻燃聚醚多元醇
1.
The high reactive flame retardant polyether polyol(HIROL) for polyurethane resin was synthesized by copolymerization of epoxy propane(EP), oxirane(EO), pentabromophenyl glycidyl ether(PBPGE) and glycerol, using BF 3·THF as catalyst.
结果表明 ,当环氧乙烷 /环氧丙烷 /五溴苯基缩水甘油醚摩尔配比为 2∶7∶1时 ,所合成的阻燃聚醚多元醇以质量分数2 3%添入国产 2 5 # PU泡沫材料原料中 ,制得的阻燃PU泡沫材料氧指数为 2 8 5 ;与质量分数为 6 %的甲基膦酸二甲酯复配使用 ,氧指数提高到 32。
2.
The flame retardant polyether polyol(HIROL) containing phosphorus was synthesized with dimethyl phosphite and high reactive chloride polyether polyol(CHIRO) which had chloromethyl group in side chain.
研究了侧链含有氯甲基的高活性氯代聚醚多元醇(CHIROL)与亚膦酸二甲酯钠盐反应,合成高活性含磷阻燃聚醚多元醇(HIROL)的方法。
3.
The new flame retardant polyether polyol was prepared using N,N bis(2 hydroxylethyl) 2,4,6 tribromoaniline as beganning material and 3 (2,4,6 tribromophenoxy)epoxypropane as flame retardant raw material.
着重考察了反应物料比、投料方式、反应时间等因素对阻燃聚醚多元醇物理性质及收率的影响。
6) polyhydric alcohol conjugate polyether
多元醇组合聚醚
补充资料：接枝聚醚多元醇
分子式：
CAS号：
性质： 是一类由通用聚醚或含有双键的聚醚在烯烃单体(如苯乙烯、丙烯腈等)和引发剂(如偶氮二异丁腈等)存在下，进行接枝共聚合(称原位聚合法反应)制备的特种聚醚多元醇。常温下为奶黄色至乳白色黏稠液体，随烯烃类单体接枝量增加，黏度增大。用于制备具有较高拉伸强度和较高压缩负荷的高回弹聚氨酯软泡，也可用于制备聚氨酯弹性体等。
CAS号：
性质： 是一类由通用聚醚或含有双键的聚醚在烯烃单体(如苯乙烯、丙烯腈等)和引发剂(如偶氮二异丁腈等)存在下，进行接枝共聚合(称原位聚合法反应)制备的特种聚醚多元醇。常温下为奶黄色至乳白色黏稠液体，随烯烃类单体接枝量增加，黏度增大。用于制备具有较高拉伸强度和较高压缩负荷的高回弹聚氨酯软泡，也可用于制备聚氨酯弹性体等。