1) catching carbon
高拉碳
1.
The production process of dephosphorization under catching carbon practice with cover of converter dropped is analyzed.
分析了转炉在降罩情况下,采用高拉碳操作转炉脱磷的生产工艺,通过采取一定的措施,有效地解决了钢水磷高及回磷问题。
2) high casting speed
高拉速
1.
Practice on extend in mold copper life of high casting speed slab caster;
延长高拉速板坯连铸机结晶器铜板寿命的实践
2.
Oscillation marks formation for slab continuous casting with high casting speed was expatiated through stress analyses of initial solidifying meniscus shell during an oscillation cycle with stabilizing casting status at 2.
0m/min拉速稳定浇铸时振动周期内弯月面初凝坯壳的受力情况,阐述了高拉速连铸坯表面振痕形成过程,给出振动参数与最大液体摩擦力和最大保护渣渣道动态压力关系;结合振动参数对振动过程参数的影响和实际设备状况,提出了振动参数优化方向,确定了拉速升至2。
3.
A physical model was established to study the mechanism of molten slag behavior in slab continuous casting mould with high casting speed and argon blowing,and the effects of operation parameters on the liquid surface level oscillation and the slag entrapment were investigated.
基于相似理论,利用物理模型研究了高拉速吹氩条件下结晶器内的卷渣行为,考察了工艺操作参数对结晶器内液面波动和卷渣行为的影响。
3) high speed
高拉速
1.
In this paper,by analyzing the requirement of high speed continuous casting mould fluxes properties,the mould fluxes were developed for NO.
根据攀钢2#板坯连铸的工艺特点,在分析了高速连铸对保护渣性能要求的基础上,研究开发出了适应高拉速浇注的连铸保护渣,工业试验结果表明,研究开发的YC-DT高拉速用连铸保护渣,在拉速≥1。
2.
In this paper,the author calculates the solidification coefficient of billet in the case of high speed,It has a practical significance to direct the selection of technological parameters of continuous casting.
计算了高拉速条件下的铸坯凝固系数 ,对于指导高效连铸工艺参数的选择有实际的意义 ,指出由于过热度的存在 ,坯壳的生长不完全服从抛物线规律及高拉速下 ,结晶体内铸坯的凝固系数较高 ,而综合凝固系数变化不
4) Ultra-Drawing
超高拉伸
5) high tensile stress
高拉应力
1.
Based on the practical investigation into the super-long prestressed concrete structures, during the course of tensioning the high tensile stress or cracks of the structural surface near anchorages, due to the lapping link of prestressed tendons, is analyzed carefully.
结合超长预应力混凝土连续结构的工程实践,本文对张拉施工时因预应力筋搭接连接构造使结构产生高拉应力或裂缝的问题进行了深入分析,结合介绍为此开发的新型锚具式连接器,提出了解决该问题的新方法。
2.
By using 10 cm×10 cm×55 cm uniaxial tension specimens with buried tensile bars, the failure of concrete under sustained high tensile stress in investigated experimentally.
用１０ｃｍ×１０ｃｍ×５５ｃｍ等截面内埋拉杆型轴向拉伸试件，进行持续高拉应力下混凝土破坏规律的试验研究。
6) high speed casting
高拉速连铸
1.
Non-sinusoidal oscillation of continuous casting mold is one of the key technologies for high speed casting with high quality.
结晶器非正弦振动是实施高拉速连铸和提高铸坯质量的关键技术。
参考词条
补充资料：马拉普拉德高碘酸盐氧化反应
分子式：
CAS号：
性质：邻二醇类化合物在水或水与有机溶剂组成的混合溶剂中与高碘酸或高碘酸钠作用，发生定量的氧化裂解反应，按照羟碳原子处于不同位置分别转化成醛、甲酸和酮。常用于定量测定和结构分析，有时也用于合成。
CAS号：
性质：邻二醇类化合物在水或水与有机溶剂组成的混合溶剂中与高碘酸或高碘酸钠作用，发生定量的氧化裂解反应，按照羟碳原子处于不同位置分别转化成醛、甲酸和酮。常用于定量测定和结构分析，有时也用于合成。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。