1) large-tow carbon fiber
大丝束碳纤维
1.
The prepreg of modification epoxy resin / large-tow carbon fiber had been analyzed using scanning electron microscope, The modification epoxy resin / large-tow carbon fiber composites capability including mechanical、toughness、hot-wet and medium had .
用红外光谱分析仪、差式扫描量热仪、动态热机械分析仪等设备分析了改性后的树脂基体，用电子扫描电镜对改性环氧树脂体系／大丝束碳纤维预浸料进行了扫描电镜分析，测试了改性环氧树脂体系／大丝束碳纤维复合材料的常规力学强度、韧性性能、耐湿热性能以及耐介质性能。
2) large tow carbon fiber prepreg
大丝束碳纤维预浸料
1.
The prepreg technology development is introduced in this paper, which is adapted to the low cost making technology of composite, It included: storable prepreg at room temperature; low temperature curing prepreg; large tow carbon fiber prepreg; Fast curing prepreg.
本文根据复合材料低成本制造技术,介绍了预浸料技术的新进展,包括可常温储存的预浸料;低温固化高温使用的预浸料;大丝束碳纤维预浸料和快速固化预浸料。
3) carbon fibrous silk
碳纤维丝
1.
Through the contrast of Carbon Fibrous cloth and carbon Fibrous Silk which are used in strengthening concrete beams,this paper mainly studies the influence of carbon fibrous silk on the flexural performance of concrete beams.
通过碳纤维丝及碳纤维布加固补强钢筋混凝土梁的对比试验,主要研究碳纤维丝对钢筋混凝土梁受弯性能的影响。
4) carbon filament
碳丝，碳纤维
6) carbon fiber precursor
碳纤维原丝
1.
Mechanical properties of carbon fiber precursors prepared from liquefied wood in phenol;
木材苯酚液化物碳纤维原丝的力学性能
补充资料：碳纤维原丝
分子式：
CAS号：
性质：又称碳纤维前驱体。指生产碳纤维用的聚合物原丝。不同的品种性能要求各异，聚丙烯腈(PAN)原丝的分子量比服用腈纶高，强度>5cN/dtex，通用级和标准级原丝也可采用纺织用大丝束。高性能品的灰分要尽可能少，为了制备高强高模碳纤维，可选用PAN与黏胶、聚乙烯醇(PVA)、聚酰亚胺等的混合原丝；沥青原丝则有各向同性、预中间相、潜在中间相和中间相之分；黏胶原丝则要求α-纤维素含量高者，长短丝皆可用；酚醛原丝在未交联处理前非常脆弱，交联后方有实用价值。制法为PAN和黏胶原丝以湿纺为主，沥青和酚醛原丝以熔纺为主。用途主要制碳纤维，PAN原丝可作石棉代用品等，酚醛纤维可作抗燃纤维。
CAS号：
性质：又称碳纤维前驱体。指生产碳纤维用的聚合物原丝。不同的品种性能要求各异，聚丙烯腈(PAN)原丝的分子量比服用腈纶高，强度>5cN/dtex，通用级和标准级原丝也可采用纺织用大丝束。高性能品的灰分要尽可能少，为了制备高强高模碳纤维，可选用PAN与黏胶、聚乙烯醇(PVA)、聚酰亚胺等的混合原丝；沥青原丝则有各向同性、预中间相、潜在中间相和中间相之分；黏胶原丝则要求α-纤维素含量高者，长短丝皆可用；酚醛原丝在未交联处理前非常脆弱，交联后方有实用价值。制法为PAN和黏胶原丝以湿纺为主，沥青和酚醛原丝以熔纺为主。用途主要制碳纤维，PAN原丝可作石棉代用品等，酚醛纤维可作抗燃纤维。