1) CASE2199(T23)steel
CASE2199(T23)钢
2) CASE2199 steel
CASE2199钢
1.
Experience in welding of CASE2199 steel;
CASE2199钢的焊接实践
3) T23 steel
T23钢
1.
Creep rupture specimens were chosen to study the effect of microstructural evolution at 550 ℃,600 ℃ and 650 ℃ on the properties of domestic-made T23 steel.
通过对国产T23钢550℃、600℃和650℃的持久试样显微组织的分析,研究了T23钢高温蠕变过程中的组织演变及其对性能的影响。
2.
Microstructure evolution and mechanical properties of domestic T23 steel aged at 600 ℃ were investigated by OM,SEM,TEM and the test of extension and impaction.
采用光学显微镜、扫描电镜、透射电镜观察和拉伸、冲击试验等方法,研究了国产T23钢在600℃时效时的组织变化和力学性能。
3.
The specimens before and after crept at 550 ℃,600 ℃and 650 ℃were chosen to study the microstructural evolution and the effect on the properties of domestic T23 steel.
通过分析T23钢常规组织状态及其在550℃、600℃、650℃高温持久试样的微观组织,研究了T23钢高温蠕变过程中的组织演变及对性能的影响。
4) T23 steel tube
T23钢管
1.
In view of the T23 steel tube bursting of Units 1 and 2 in Zhuhai Power Station,the microstructure,mechanical property,Vickers hardness,anti-steam-oxidation performance of T23 steel tubes are tested and analyzed.
针对珠海电厂1号、2号机组T23钢管出现爆管现象,对T23钢管的显微组织、力学性能、维氏硬度、抗蒸汽氧化性能进行了测试和分析,指出长期超高温运行是T23钢管爆管的主要原因,为此,提出相应的防范措施,对今后该种管材在超(超)临界机组的大范围应用提供参考和借鉴。
5) T23(P23) steel
T23(P23)钢
6) T23 heat-resistance steel
T23耐热钢
1.
Taking FeNiCrSiB amorphous alloy as interlayer in argon atmosphere,the T23 heat-resistance steel pipes were jointed by transient liquid-phase bonding using two-step heating process in argon atmosphere: bonded at 1240℃ for 50 s,and isothermal congealed at 1210℃ for 4 min.
用FeNiCrSiB合金箔作中间层,氩气保护,在焊接双温工艺(加热温度1240℃,保温50 s,等温凝固温度1210℃,保温4 min,压力6 MPa)条件下,对T23耐热钢管进行TLP连接。
补充资料：catalyst case(reactor)
分子式：
CAS号：
性质：指装有催化剂的催化反应器。根据催化剂的运动状态，可分为固定床，流化床和移动床反应器。根据物料与催化剂的物相，可分为气-液；气-固；液-固和三相床反应器。根据操作方式可分为间歇、连续或周期反应器。根据反应器型式可分为釜式及管式反应器等。
CAS号：
性质：指装有催化剂的催化反应器。根据催化剂的运动状态，可分为固定床，流化床和移动床反应器。根据物料与催化剂的物相，可分为气-液；气-固；液-固和三相床反应器。根据操作方式可分为间歇、连续或周期反应器。根据反应器型式可分为釜式及管式反应器等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条