1) disbonded holiday
剥离涂层缺陷
2) disbonded coating
剥离涂层
1.
Buried pipeline are routinely protected by the synergistic effect of coatings and cathodic protection(CP),however,corrosion often occurs under disbonded coatings.
综述了在有阴极保护的条件时剥离涂层下缝隙内电位电流的分布和化学环境的变化、阴极保护防止缝隙腐蚀的机理、微生物腐蚀的机理以及前人提出的关于剥离涂层下微生物腐蚀与阴极保护相互作用的规律,并展望了对于解决剥离涂层下微生物腐蚀难题需进一步的实验研究。
3) wipe off
涂层剥离
4) coating defect
涂层缺陷
1.
The effect of coating defect on the permeation behavior of corrosive ions through coatings,coatings degradation,the corrosion behavior of substrates are discussed based on the review of the study field which included coating defects,blistering and wet adhesion etc.
通过对涂层缺陷、涂层起泡、湿附着力等研究领域的回顾 ,讨论了涂层缺陷对腐蚀性介质离子在涂层中的传输行为、涂层失效、基体腐蚀行为等方面的影响。
5) coating defects
涂层缺陷
1.
The influence of soil resistivity and coating defects on IR drop error in cathodic protection(CP)potential measurement was studied by theoretical methods.
理论分析土壤电阻率和涂层缺陷电阻等参数对埋地管道阴极保护电位测量时IR降误差的影响 ,建立IR降电阻因子计算模型 ,并用实验数据验证 ,此外 ,还讨论了IR降误差的工程预测方法 。
6) coating strip force
涂层剥离力
补充资料：涂层剥离强度
分子式：
CAS号：
性质：又称涂层剥离强度。系利用无机溶剂型黏合剂，将按规定切取的革试样的有涂层一面粘贴的黏合板上，革样的两端各超出黏合板15mm（自由端），将黏合板连同革样固定在拉力机上，机上的试样夹夹住革样的一端，并挂在拉力钩上，开动拉力机至皮革涂饰层剥离至规定的长度（30～35mm），记录拉力机上所示的力矩图，从该力矩图上计算出涂层的30～35mm长的皮革试样上的黏着力的平均值，作为黏着牢度，以N/10mm表示。
CAS号：
性质：又称涂层剥离强度。系利用无机溶剂型黏合剂，将按规定切取的革试样的有涂层一面粘贴的黏合板上，革样的两端各超出黏合板15mm（自由端），将黏合板连同革样固定在拉力机上，机上的试样夹夹住革样的一端，并挂在拉力钩上，开动拉力机至皮革涂饰层剥离至规定的长度（30～35mm），记录拉力机上所示的力矩图，从该力矩图上计算出涂层的30～35mm长的皮革试样上的黏着力的平均值，作为黏着牢度，以N/10mm表示。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。