1) fired magnesia-calcium brick
烧成镁钙砖
1.
The production and application status of magnesite-dolomite refractories such as fired magnesia-calcium brick,unburned magnesia-calcium(carbon) brick and Mg-Ca coating mixture for tundish etc are introduced and it is pointed out that magnesite-dolomite refractories should be developed on high CaO content,high grade,seriation and non-shaped refractories in the near future.
介绍了我国烧成镁钙砖、不烧镁钙(碳)砖和镁钙质中间包涂料等镁钙质耐火材料的生产和使用现状,指出今后我国的镁钙质耐火材料应向高CaO含量、高档次、系列化和不定形方向发展。
2) burned-magnesia brick
烧成镁砖
1.
We found the reasons that a lot burned-magnesia brick is scrapped because of split by delve into the production technology.
通过对烧成镁砖生产工艺的深入研究,找到了烧成镁砖批量开裂报废的原因,并通过一系列的试验工作,找到了解决方案,即通过加入"复合结合剂"来有效地杜绝制品烧后开裂现象,而且"复合结合剂"的加入没有降低制品的理化性能。
3) unfired magnesia-calcium brick
不烧镁钙砖
1.
The unfired magnesia-calcium brick has been developed and used in 90t LF refining furnace in centain steelplant.
以合成镁钙砂、电熔镁砂为原料,以无水树脂做结合剂,添加适量的添加剂,研制出了LF精炼炉用不烧镁钙砖。
4) unburned magnesia-calcium(carbon) brick
不烧镁钙(碳)砖
5) Unburned MgO-CaO-C brick
不烧镁钙炭砖
6) magnesia-calcia-alumina brick
镁钙铝砖
补充资料：镁钙砖
分子式：
CAS号：
性质：又称高钙镁砖。以方镁石为主晶相，以硅酸三钙为次晶相的镁质耐火材料。含MgO80%～87%，CaO6%～9%，CaO/SiO2比在 2.2～3.0之间。其显显结构特征为方镁石与硅酸二钙及硅酸三钙直接接触，低共熔物（4CaO·Al2O3·Fe2O3成细脉状填充于硅酸二钙和硅酸三钙的晶隙间。气孔率低。荷重软化开始温度一般高于1700℃，抗碱性渣性能良好。但抗热震性较差。以钙镁砂为原料，经粉碎、配料、混炼、成型后，在1550～1600℃高温下烧成。可用于炼钢侧吹转炉风眼处、平炉炉顶和吹氧转炉上等处。
CAS号：
性质：又称高钙镁砖。以方镁石为主晶相，以硅酸三钙为次晶相的镁质耐火材料。含MgO80%～87%，CaO6%～9%，CaO/SiO2比在 2.2～3.0之间。其显显结构特征为方镁石与硅酸二钙及硅酸三钙直接接触，低共熔物（4CaO·Al2O3·Fe2O3成细脉状填充于硅酸二钙和硅酸三钙的晶隙间。气孔率低。荷重软化开始温度一般高于1700℃，抗碱性渣性能良好。但抗热震性较差。以钙镁砂为原料，经粉碎、配料、混炼、成型后，在1550～1600℃高温下烧成。可用于炼钢侧吹转炉风眼处、平炉炉顶和吹氧转炉上等处。