1) Titania modified MCM 41
MCM-TiO2
2) Pd deposited titania modified MCM 41
Pd/MCM-41-TiO2
3) titanium dioxide
TiO2
1.
Recently the progress has been made in the area of controlling and manipulating photon with photonic crystal of titanium dioxide.
最近利用TiO2光子晶体控制光子的研究取得了一定进展。
2.
Flaky titanium dioxide was prepared by the sol-gel method using Ti(OC4H9)4.
以Ti(OC4H9)4为原料,采用溶胶-凝胶涂膜法制备片状TiO2,探讨了溶胶的性质、涂膜过程、煅烧温度等参数对片状TiO2性能的影响,结果表明:反应温度为30℃,水与Ti(OC4H9)4的摩尔比为2-4, Ti(OC4H9)4与无水乙醇的摩尔比为7-10,pH值为1-3,反应时间为15 min的条件下,通过溶胶涂膜、干燥、剥片及400℃煅烧2 h,可得到具有明显片状结构的TiO2。
3.
The titanium dioxide(TiO2) based photocatalysts were prepared on the adsorption layer of the zeolite which acted as a "nanreactor".
以钛酸丁酯为钛源,天然沸石为载体,采用吸附相反应技术,以沸石表面吸附的水层为"纳米反应器",制备了沸石/TiO2光催化剂。
4) Titania
[英][tai'teiniə] [美][taɪ'tenɪə]
TiO2
1.
In order to obtain visible light response,doping or modifying titania by nonmetal elements such as nitrogen has been investigated extensively in recent years.
为了扩展TiO2光催化剂对可见光的利用,以非金属元素对其进行掺杂和改性是近年来很活跃的研究内容,文献报道主要有氮、碳、硫、氟等非金属元素的改性结果。
2.
The nitrogen doped titania photocatalysts were prepared by nitridation process.
采用氨气氮化工艺制备了氮掺杂的TiO2光催化剂,研究了氮化温度对光催化性能的影响。
3.
The paper reviews the types of core-shell titania composite nanoparticles,their.
本文着重介绍核壳型TiO2的几种类型、特点及其性能,并提出其今后的发展方向。
5) TiO_2
TiO2
1.
Low temperature RF magnetic sputtering is applied to deposit nano-structured film of TiO_2 and rare-earth Nd on the surface of PET nonwoven.
采用低温射频磁控溅射技术在PET基非织造布表面沉积TiO2与稀土Nd的纳米结构复合薄膜,以宽化纳米TiO2的吸收光谱,使其在可见光照射的情况下具有较好的抗菌效果,实现纺织材料表面的抗菌功能化。
2.
Effects of reaction pH,E2 concentration,applied TiO_2 dose,UV light power,H_2O_2,O_3 were investigated respectively.
以低压汞灯为光源,采用间歇式光氧化反应器,研究了17β-雌二醇(E2)在纳米TiO2(Degussa P-25)悬浆体系中的光催化降解。
3.
TiO_2/zeolite 4A and TiO_2/vermiculite composites were prepared by sol-gel technique with tetrabutyl titanate as the titanium source,and zeolite 4A and natural layered vermiculite as the supports.
以4A沸石和天然蛭石为载体,钛酸四丁酯为钛源,采用溶胶-凝胶法制备了TiO2/4A沸石和TiO2/天然蛭石光催化复合材料,研究了复合材料对偶氮染料甲基橙的暗态吸附规律和光降解性能。
6) TiO 2
TiO2
1.
The crystal structure and electronic band structure of undoped and Fe-doped anatase TiO 2 have been investigated by using the plane-wave ultrasoft pseudopotential method in the generalized gradient approximation (GGA).
采用平面波超软赝势方法研究了锐钛矿型TiO2 及Fe掺杂TiO2 的晶体结构和能带结构 ,计算表明Fe掺杂导致TiO2 电子局域能级的出现及禁带变窄 ,从而导致吸收光谱红移 。
2.
Effects of the amou nt of wat er and acid used for the preparation of TiO 2 sols,the —COOH content in the ac ry lic resin and preparing methods on the structure of hybrid materials were invest igated.
通过预水解的二氧化钛(TiO2 )溶胶与丙烯酸树脂共混或原位聚合的方法制备了均匀透明的丙烯酸树脂 TiO2 有机 无机杂化材料。
3.
It is shown that the cosmetics containing title compound have greater superiority than that using montmorillonite or TiO 2 alone.
通过钛交联蒙脱石的各个成分在化妆品中所起的作用,论述了钛交联蒙脱石纳米复合材料在化妆品应用中具有防晒、保湿、去除异味、增稠等多种功效,比单独使用TiO2 和蒙脱石具有更大的优越性。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条