2) particle reinforced 6066/SiC composites
颗粒增强6066/SiC复合材料
1.
The elastic modulus(E_c) of SiC particle reinforced 6066/SiC composites made by powder metallurgy and sprayed deposition were measured by dynamic elastic modulus tester.
利用动态弹性模量测试仪测试采用粉末冶金和喷射沉积方法制备的SiC颗粒增强6066/SiC复合材料的弹性模量Ec。
4) SiC particle reinforced aluminium matrix composites
SiC颗粒增强铝基复合材料
1.
Based on reviewing the applications and machining of particle reinforced metal matrix composites,the high-speed cutting performance of SiC particle reinforced aluminium matrix composites is analyzed through the milling experiments.
从颗粒增强金属基复合材料的应用和切削加工现状出发 ,针对SiC颗粒增强铝基复合材料的高速切削加工性能进行了试验分析。
2.
In this paper,the high-speed cutting performance of SiC particle reinforced aluminium matrix composites is analyzed through the milling experiments.
对SiC颗粒增强铝基复合材料的高速切削加工性能进行了试验分析,研究了铣削速度对铣削力、切削温度、加工表面粗糙度、表面形貌和刀具磨损的影响,从而获得了能够保证对其进行高效率、高精度加工的合理工艺参数。
5) SiC particle reinforced metal matrix composites
SiC颗粒增强金属基复合材料
补充资料：碳化硼颗粒增强镁基复合材料
分子式：
CAS号：
性质：用碳化硼颗粒增强镁合金基体的镁基复合材料。随着碳化硼颗粒的加入和含量的增加，镁基复合材料的比强度、比模量、耐磨性有大幅度的提高，颗粒含量一般为10％～25％，也可达65％，含量在25％以下进行挤压加工成各种型材、棒材。性能明显优于镁合金。如Mg9％Al0.15Mn合金，用25％的碳化硼颗粒增强制成的挤压棒材，其屈服强度为460MPa，弹性模量为91GPa，比镁合金高一倍。这种复合材料主要用于航空、航天、先进武器等结构件。
CAS号：
性质：用碳化硼颗粒增强镁合金基体的镁基复合材料。随着碳化硼颗粒的加入和含量的增加，镁基复合材料的比强度、比模量、耐磨性有大幅度的提高，颗粒含量一般为10％～25％，也可达65％，含量在25％以下进行挤压加工成各种型材、棒材。性能明显优于镁合金。如Mg9％Al0.15Mn合金，用25％的碳化硼颗粒增强制成的挤压棒材，其屈服强度为460MPa，弹性模量为91GPa，比镁合金高一倍。这种复合材料主要用于航空、航天、先进武器等结构件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。