1.
Sustaining tensile tests are carried out till the specimens fail by combining differenttemperatures and stresses over the range of 760 - 1050℃ and 750 - 140 MPa on nickel-base singlecrystal superalloy CMSX-2.
在760－1050℃和750－140MPa范围内，选择不同温度和应力的配合对CMSX－2合金进行持久拉伸至断裂，观察了试件原始树枝状晶各区域（枝晶干、枝晶臂及枝晶间）中γ’相的定向粗化及合金元素的分布特征结果表明，γ’的走向粗化程度在枝晶干内最大，在枝晶臂内次之，在枝晶间最小。
4) single crystal nickel base superalloys
单晶镍基合金
1.
The affection factors of the creep behaviour for two single crystal nickel base superalloys with [001] orientation were studied by measuring the creep curves and internal stress of dislocation motion, and by EDAX composition analysis as well.
通过对 [0 0 1 ]取向单晶镍基合金蠕变曲线和位错运动内摩擦力的测定及能谱微区成分分析 ,研究了两种合金的蠕变特性。
6) nickel-base single crystal superalloy
镍基单晶超合金
1.
Void growth behavior plays an important role in the deformation, damage and rupture of the nickel-base single crystal superalloys at high temperature.
在高温状态下,镍基单晶超合金的变形、损伤及断裂分析中,孔洞的长大都起着主要的作用。
补充资料：镍基单晶高温合金
镍基 单 晶 高温合金具有优良的高温性能，是目前制造先进航空发动机和燃气轮机叶片的主要材料。为了满足高性能航空发动机的设计需求，多年来，各国十分重视镍基单晶高温合金的研制和开发。20 世 纪 80年代以来，单晶高温合金一直沿着其独特的道路发展。随着合金设计理论水平的提高和生产工艺的改进，相继出现耐温能力比第1代单晶合金分别大约高30℃和60℃的第2代单晶合金和第3代单晶合金;第2代单晶高温合金的代表有pwa1484(') ,c msx一4(2).等，第3代单晶高温合金的代表有cmsx一loll',cm sx一11(0),r e nen6(5)等。研究表明[(6)，第3代单晶高温合金cmsx一10的耐温能力比第2代单晶合金cmsx -4(最高使用温度约(1163cc)的大约高3090，其使用温度可达1204℃左右，同时，还具有十分明显的蠕变强度优势。近年来出现的第4代单晶合金rr3010的承温能力达到11800c('1，用在英国rr公司最新研制的trent发动机上。re的加入以及hf,y ,la ,ru 等元素的合理应用，使新的单晶合金的持久性能和抗环境性能均有明显的提高。