1) textile coating agent
织物涂层剂
1.
A self crosslinking textile coating agent was synthesized by means of seeded emulsion copolymerization, for which butyl acrylate(BA), ethyl acrylate(EA), hydrogen containing polymethylsiloxane(PHMS), methyl methacrylate(MMA) and acrylonitrile(AN) were selected as main monomers, and acrylic acid(AA) as functional monomer, N hydroxymethylacrylamide(NMA) as cross linking agent.
以丙烯酸丁酯 ( BA)、丙烯酸乙酯 ( EA)、含氢聚甲基硅氧烷 ( PHMS)、甲基丙烯酸甲酯 ( MMA)、丙烯腈( AN)为主单体 ,丙烯酸 ( AA)等为功能单体 ,N 羟甲基丙烯酰胺 ( NMA)等为交联剂 ,采用种子乳液共聚法制备了自交联织物涂层剂。
2) cotton fabric coating
棉织物涂层剂
1.
The effects of high hydrogen containing poymethylsiloxane amount, quantity ratio of soft and hard acrylate monomer, cross linking amount on the properties of the copolymer emulsion as cotton fabric coating were discussed.
用单体乳液滴加法合成了聚甲基硅氧烷 /聚丙烯酸酯类共聚乳液 ,探讨了高含氢聚硅氧烷用量、丙烯酸酯软硬单体的质量比、交联剂用量对其共聚乳液作为棉织物涂层剂的性能影响。
3) Coated fabric
涂层织物
1.
Research on the tensile capability of coated fabrics for air-tightness;
气密性涂层织物的拉伸性能探讨
2.
Study on the breathable treatment of microcapsule technique applying to the coated fabric;
微胶囊的制备及其在涂层织物透气整理上的应用
3.
Composite analysis of polyester/cotton coated fabric;
涂层织物分析前的涂层去除方法
4) coated fabrics
涂层织物
1.
In this paper, the relationship between the wrap single-rip tearing strength and the yarn tensile properties as well as fabric structure is studied by multi-variable linear regression for the eighteen kinds of PU coated fabrics with different specifications.
对18种不同规格基布的聚氨酯涂层织物,用一般多元线性回归和逐步回归方法,研究了纱线性能和织物结构指标等因素与单缝法撕裂强力间的关系。
2.
Moreover, the influences of coating processing on tearing strength and tearing failure mechanism were studied, and a mechanical model expressing trapezoid tear strength of coated fabrics is also proposed.
对12种不同规格的涂层织物,采用4种不同撕裂方法进行撕裂强力的测定,得到了不同撕裂方法测得的撕裂强力之间的相关关系,同时讨论了涂层及涂层工艺对织物撕裂强力的影响。
5) coating fabric
涂层织物
1.
Qualitative analysis of coating fabrics;
涂层织物组分定性分析法
2.
Be aimed at the deep colour polyester PU coating fabric,compared several kinds of dyeing auxiliaries and finishing technologies,got the best finishing effect,made the fabric has high fastness.
针对深色涤纶PU涂层织物,通过比较多种染化料助剂和整理工艺,得到最优整理效果,赋予织物较优良的色牢度。
6) fabric coating
织物涂层
1.
A fabric coating absorbing material(FCAM) with multi-layer structure was prepared on non-woven fabrics.
以无纺布为基材,采用叠层式结构制备无纺布织物涂层吸波材料。
补充资料:涂层织物
涂层织物
Coated Fabrics
第16卷涂层织物tu规的聚醋型聚氨酷,在雨水和阳光的作用下,容易发生水解反应而使油槽的使用寿命缩短,加入的抗水解助剂芳香族聚碳二亚胺易被油所萃取,所装油料挥发性低,损坏的现场更加明显,尚需改进。 涂层织物制作防护服,以不同材料取得不同的防护功能。例如,聚氯乙烯涂层织物,对飞溅的酸、碱等化学药品有很好的遮蔽作用;对接触油类和有机溶剂的工作,则用氯丁橡胶、丁腊橡胶、氯磺化聚乙烯或聚氨醋涂层的聚酞胺纤维、聚酷纤维织物;有燃烧危险的场合,热塑性纤维有可能熔融粘结在皮肤上,要改用耐高温的芳族聚酸胺纤维、粘胶纤维、改性聚丙烯睛纤维制成的底布,同时在涂层剂中加阻燃剂。 金属化织物[ls〕是在织物表面喷涂金属,以增强反射电磁波的能力,例如,作为接近火焰的工作服(炼钢、消防)依靠光亮的金属表面,把拨溅的金属熔滴和火焰的辐射热反射掉;长期在阴极射线管或高压输电线路附近的工作人员,穿上金属化织物可以减少电子辐射的伤害;由于金属化织物有异电性能,可制成抗静电服,用于静电可能造成灾害的工作环境。5.安全与环境保护 涂层加工,由于大量使用溶剂,溶剂蒸气有害于工人的健康,同时污染环境.使涂层加工厂‘受到多方面的制约和舆论的谴责;有机溶剂的易燃易爆性,使用溶剂的车间(仓库、运输工具等)必须有特殊的消防措施。 表1列出涂层常用的几种溶剂性能。乙酸乙醋等溶剂沸点闪点都很低,爆炸下限也很小,因此要注意防火,防火的关键部位是烘箱。涂层后织物进人烘箱,烘箱内热空气吹拂织物表面,促使溶剂快速蒸发。为了保持烘箱内温度的稳定,热空气是循环使用的,只让其中一部分(废气)排放,因此热空气中溶剂含量很高,涂层工作者应实地测定排出废气量及其中溶剂含量,经济合理地调整工艺参数,务必使浓度远离爆炸下限。 为保证安全,使用溶剂的车间应按防爆车间处理,与其他车间之间应有隔离通道,车间内设施应符合有关条例规定。 在车间中弥漫的溶剂,含量一般远低于烘箱中,但浓度过高将损害操作人员的健康。其中二甲基甲酞胺毒性较大,在空气中允许含量远低于其他溶剂,因而是控制的重点。在有害气体含量较高的工作点,应加装捕集罩,或地面吹扫,以降低浓度。 为了使排出废气符合环境保护的法规,一般是在涂层机__L附加污染控制设备,如活性炭吸附、水淋洗涤废气等办法,由于大多数溶剂的水溶性很小,要改变涂层剂的溶剂系统,用水溶性大的二甲基甲酞胺代替其他溶剂。或使用氧化装置,使废气中的溶剂氧化分解而消除毒性。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。