说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 硼砂盐浴渗铬
1)  borax salt bath chromizing
硼砂盐浴渗铬
2)  VANADIZING IN THE SALT BATH WITH LOW CONTENT OF BORAX
低硼砂盐浴渗钒
3)  borax bath
硼砂盐浴
1.
The influece of reducer on coating of Cr12MoV steel was studied by TD process using a borax bath.
采用硼砂盐浴的方法进行TD处理实验,研究了还原剂对Cr12MoV钢TD处理的影响。
4)  salt-bath chromizing
盐浴渗铬
1.
Effect of salt-bath chromizing process on microstructure and properties of chromized layer;
T12钢盐浴渗铬工艺对渗层组织和性能的影响
2.
Effects on 45 & T10A steel in different process time of salt-bath chromizing adding rare-earth were studied.
在相同温度下,对45钢和T10A钢进行不同时间的稀土盐浴渗铬,结果表明:随着渗铬时间的延长,渗铬的效果,在总体上呈增加的趋势,45钢在4h就可以达到较好效果,而T10A钢则在6h达到较好效果。
5)  low temperature salt bath chromizing
低温盐浴渗铬
1.
The results showed that a chromized layer with good wear resistance could be gained in steel 45 by low temperature salt bath chromizing.
研究了 45钢低温盐浴渗铬工艺 ,分析了渗铬层的金相组织和相结构 ,测量了渗层厚度、渗层硬度及铬浓度分布 ,并进行了渗铬层的耐磨试验。
2.
The microstructure ,phase make up,chromium thickness,microhardness and corroding resistance of low temperature salt bath chromizing layers of steel Q235,45 and T10 are contrasted.
通过 Q2 35钢、45钢、T1 0钢低温盐浴渗铬层的金相组织、相结构、厚度、铬浓度、显微硬度和耐蚀性的对比 ,表明碳含量越高 ,铬碳化合物层越厚 ,显微硬度越高 ,耐蚀性越好。
3.
Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied.
研究了 T10钢在低温盐浴渗铬后直接淬火并回火工艺。
6)  boronchromizing
硼铬共渗
1.
The microstructure and property of boronchromizing coating on 3Cr13 stainless steel have been investigated.
本文研究了3Cr13钢硼铬共渗层的组织和性能共渗层是由含铅量较高的(Fe,Cr)2B相组成。
补充资料:无水硼砂
分子式:
CAS号:

性质:见无水四硼酸钠。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。