1) aging treating after welding
焊后时效处理
3) post-weld treatment Talk about Application Spray
焊后处理
4) post welding heat treatment
焊后热处理
1.
This study is concerned with the effect of post welding heat treatment(PWHT)on the microstructure and properties at the intercritical reheated coarse-grained heat-affected zone(IRCGHAZ)of WB36 steel, and investigated whether the PWHT could reduce IRCGHAZ embrittlement.
针对WB36钢(15NiCuMoNb5)临界再热粗晶区(IRCGHAZ)存在的脆化现象,研究了焊后热处理对模拟临界再热粗晶区(IRCGHAZ)组织性能的影响,探讨其改善韧性作用。
2.
This paper studies the technology,equipment and properties of post welding heat treatment of the RE microalloy quenching rail which was heated with medium frequency induction and quenched with pressure air for head of,normalized for other of.
通过热模拟试验选择了合理的焊后热处理工艺参数，恢复了轨头强度和硬度，并大幅度地提高了焊接接头的韧塑性和综合性能，满足了无缝线路铺设使用要求。
3.
It is pointed out that post welding heat treatment will not significantly improve residual stress in dissimilar steel welding joints unless correct and appropriate heat treatment procedures are taken.
文章主要讨论了焊接热处理对火电站管道异种钢焊接接头带来的问题,分析了热处理对接头组织、焊接残余应力的影响,指出通过焊后热处理可以明显改善电厂管道异种钢焊接接头残余应力,但要使用正确和合适的热处理工艺。
5) postweld heat treatment
焊后热处理
1.
Effect of postweld heat treatment on microstructure of electron beam welded joints of Ti_3Al;
焊后热处理对Ti_3Al电子束焊缝组织形态的影响
2.
Numerical value analysis on reduction of welding residual stresses with postweld heat treatment on P91 pipes;
焊后热处理消除P91钢管焊接残余应力的数值分析
3.
Based on Barkhausen Noise,as-welded residual stresses and residual stress after postweld heat treatment of 16MnR(include weld- ing metal,fusion zone,heat affect zone)were measured by using magneto-elastic method with 20～70 kHz frequency & 0.
07mm的STRESS- CAN500C磁弹性应力仪,测量了压力容器用16MnR钢焊后以及焊后热处理的残余应力(包括焊缝、熔合区、热影响区),研究了残余应力的形成、不同区域的分布。
6) Post weld heat treatment
焊后热处理
1.
The application and requirement of post weld heat treatment used by spherical tanks are summarized.
概述了球罐的应用及对焊后热处理的要求,详细介绍了国内球罐热处理技术的新进展,包括电加热法、爆炸法、内燃法、电加热辅助燃油法,还展望了该领域技术的发展前景。
2.
The influence of different post weld heat treatment conditions on the microstructures and mechanical properties of friction welded joints between drill pipe DZ60 steel and its tie in 40Cr steel has been discussed.
同时发现 ,采用合适的焊后回火热处理温度 ,可以有效提高焊接接头的抗拉强度及屈服强度 ,使其各项力学性能达到DZ6 0钻杆管材的技术标准 ,从而有效减少地质钻杆摩擦焊接头焊后热处理工艺 ,降低制造成
3.
The effect of post weld heat treatment on the impact toughness in inertia friction welded joints of carbon steel was studied in this paper The result show that the post weld heat treatment greatly affected the impact toughness of inertia friction welded joints The impact toughness of the welded joints can be improved by an adequate post weld heat treatmen
研究了焊后热处理对碳钢惯性摩擦焊接头冲击韧性的影响。
补充资料：金属热处理:时效处理
将淬火后的金属工件置於室温或较高温度下保持适当时间﹐以提高金属强度的金属热处理工艺。室温下进行的时效处理是自然时效﹔较高温度下进行的时效处理是人工时效。在机械生產中﹐为了稳定铸件尺寸﹐常将铸件在室温下长期放置﹐然后才进行切削加工。这种措施也被称为时效。但这种时效不属於金属热处理工艺。
20世纪初叶﹐德国工程师A.维尔姆研究硬铝时发现﹐这种合金淬火后硬度不高﹐但在室温下放置一段时间后﹐硬度便显著上昇﹐这种现象后来被称为沉淀硬化。这一发现在工程界引起了极大兴趣。随后人们相继发现了一些可以採用时效处理进行强化的铝合金﹑铜合金和铁基合金﹐开创了一条与一般钢铁淬火强化有本质差异的新的强化途径──时效强化。
绝大多数进行时效强化的合金﹐原始组织都是由一种固溶体和某些金属化合物所组成。固溶体的溶解度随温度的上昇而增大。在时效处理前进行淬火﹐就是为了在加热时使儘量多的溶质溶入固溶体﹐随后在快速冷却中溶解度虽然下降﹐但过剩的溶质来不及从固溶体中分析出来﹐而形成过饱和固溶体。为达到这一目的而进行的淬火常称为固溶热处理。
经过长期反復研究证实﹐时效强化的实质是从过饱和固溶体中析出许多非常细小的沉淀物颗粒(一般是金属化合物﹐也可能是过饱和固溶体中的溶质原子在许多微小地区聚集)﹐形成一些体积很小的溶质原子富集区。
在时效处理前进行固溶处理时﹐加热温度必须严格控制﹐以便使溶质原子能最大限度地固溶到固溶体中﹐同时又不致使合金发生熔化。许多铝合金固溶处理加热温度容许的偏差只有5℃左右。进行人工时效处理﹐必须严格控制加热温度和保温时间﹐才能得到比较理想的强化效果。生產中有时採用分段时效﹐即先在室温或比室温稍高的温度下保温一段时间﹐然后在更高的温度下再保温一段时间。这样作有时会得到较好的效果。
马氏体时效钢淬火时会发生组织转变﹐形成马氏体。马氏体就是一种过饱和固溶体。这种钢也可採用时效处理进行强化。
低碳钢冷态塑性变形后在室温下长期放置﹐强度提高﹐塑性降低﹐这种现象称为机械时效。
20世纪初叶﹐德国工程师A.维尔姆研究硬铝时发现﹐这种合金淬火后硬度不高﹐但在室温下放置一段时间后﹐硬度便显著上昇﹐这种现象后来被称为沉淀硬化。这一发现在工程界引起了极大兴趣。随后人们相继发现了一些可以採用时效处理进行强化的铝合金﹑铜合金和铁基合金﹐开创了一条与一般钢铁淬火强化有本质差异的新的强化途径──时效强化。
绝大多数进行时效强化的合金﹐原始组织都是由一种固溶体和某些金属化合物所组成。固溶体的溶解度随温度的上昇而增大。在时效处理前进行淬火﹐就是为了在加热时使儘量多的溶质溶入固溶体﹐随后在快速冷却中溶解度虽然下降﹐但过剩的溶质来不及从固溶体中分析出来﹐而形成过饱和固溶体。为达到这一目的而进行的淬火常称为固溶热处理。
经过长期反復研究证实﹐时效强化的实质是从过饱和固溶体中析出许多非常细小的沉淀物颗粒(一般是金属化合物﹐也可能是过饱和固溶体中的溶质原子在许多微小地区聚集)﹐形成一些体积很小的溶质原子富集区。
在时效处理前进行固溶处理时﹐加热温度必须严格控制﹐以便使溶质原子能最大限度地固溶到固溶体中﹐同时又不致使合金发生熔化。许多铝合金固溶处理加热温度容许的偏差只有5℃左右。进行人工时效处理﹐必须严格控制加热温度和保温时间﹐才能得到比较理想的强化效果。生產中有时採用分段时效﹐即先在室温或比室温稍高的温度下保温一段时间﹐然后在更高的温度下再保温一段时间。这样作有时会得到较好的效果。
马氏体时效钢淬火时会发生组织转变﹐形成马氏体。马氏体就是一种过饱和固溶体。这种钢也可採用时效处理进行强化。
低碳钢冷态塑性变形后在室温下长期放置﹐强度提高﹐塑性降低﹐这种现象称为机械时效。