2) High-carbon fly-ash brick
高碳粉煤灰砖
4) decarburized fly ash
脱碳粉煤灰
1.
The results show that it is feasible to prepare the brick by decarburized fly ash containing flotation reagent.
实验结果表明:含有残留浮选药剂的脱碳粉煤灰制备蒸压砖是可行的,当脱碳粉煤灰掺入量70%,磷石膏掺入量3%时,在自然养护3 d,蒸压温度200℃,保温时间10 h的工艺条件下制备蒸压砖,该制品抗压强度为17。
5) high-alumina fly ash
高铝粉煤灰
1.
The preparation of β-Sialon powder from high-alumina fly ash:an experimental study;
利用高铝粉煤灰合成β-Sialon粉体的实验研究
2.
Minerals in feed coal and their contribution to high-alumina fly ash in the Jungar Power Plant;
准格尔电厂炉前煤矿物组成及其对高铝粉煤灰形成的贡献
3.
Mineral abundances of high-alumina fly ash from the Jungar Power Plant,Inner Mongolia,China;
内蒙古准格尔燃煤电厂高铝粉煤灰的矿物组成与特征
6) high-calcium fly ash
高钙粉煤灰
1.
Research on using high-calcium fly ash as the hardening agent of soft soil;
利用高钙粉煤灰做软粘土固化剂
2.
Study on volume stability control of cement paste with large amount of high-calcium fly ash;
大掺量高钙粉煤灰水泥浆体体积安定性控制研究
3.
Effects of slag,high-calcium fly ash,desulfurized gypsum,calcined desulfurized gypsum and sodium sulfate on early age autogenous shrinkage of cement pastes,long terms of desiccation shrinkage and initial cracking sensitivity of cement mortar are researched.
0%(质量分数,下同)矿粉和高钙粉煤灰等量替代水泥对水泥净浆早期自收缩性能的影响及水泥砂浆的长期干燥收缩性能和初始开裂敏感性。
补充资料：粉煤灰硅酸盐水泥
分子式：
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。
CAS号：
性质：由硅酸盐水泥熟料、粉煤灰、适量石膏磨细制成的水硬性胶凝材料，代号P·F，中国主要水泥品种之一。粉煤灰掺加量为20％～40％(wt)，标号分275、325、425、425R、525、525R、625R七个等级。性能和火山灰水泥相似，但需水性及干缩性较小，抗裂性较好，水化热较低，抗蚀性也较好。适用于一般的工业和民用建筑，尤其适用于大体积水工混凝土以及地下和海港工程等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。