1) Al/Fe molar ratio
Al/Fe mol比
2) Mol (Fe/P)
Mol(Fe/P)
3) Fe-Al coating
Fe-Al涂层
1.
Al/Ni coating and Fe-Al coating using for the bonding coaling were obtained by plasma spraying.
用等离子喷涂技术制备了用作粘结底层的Al/Ni、Fe-Al涂层,研究对比了这两种涂层在锌液中的耐腐蚀性能。
2.
Results show that with the increasing of temperature,the corrosion rate of all Fe-Al coatings also increased,the corrosion resistance of the Fe-Al coating with addition of Cr3C2 is superior to those without or with addition of WC.
结果表明:随温度升高,4种Fe-Al涂层的腐蚀增重都增加,添加Cr3C2比添加WC或不添加任何增强的Fe-Al涂层有更高的耐腐蚀性。
4) Fe/Al interface
Fe/Al界面
1.
DFT of first-principles was used to study the energy and electronic structure Fe/Al interface.
利用第一性原理中的DFT理论研究了Fe/Al界面的能量学和电子结构,讨论了替位型掺杂的元素Zn、Mn、Ni在Fe/Al界面处的作用。
5) Al-Fe alloy
Al-Fe合金
1.
To investigate the effect of an alternating magnetic field on the morphology and distribution of iron-containing intermetallic phases in Al-Fe alloy,the near eutectic Al-1.
研究了交流磁场对Al-Fe合金中含铁相形态及分布的影响。
2.
In order to solve the problems of the primary Fe-rich phase separating the metal matrix seriously and deteriorating the property of hypereutectic Al-Fe alloy, rare earth (Y) metal was used to modify Al-5%Fe alloy.
针对普通熔铸条件下过共晶Al-Fe合金中初生富铁相严重割裂基体、恶化合金性能的问题,采用稀土元素Y对Al-5%Fe合金进行变质处理。
6) Fe-Al/Cr_3C_2
Fe-Al/Cr3C2
补充资料：P-B比
分子式：
CAS号：
性质：金属与氧结合在金属表面生成的氧化物膜中的每个金属离子体积与金属中的每个金属原子体积之比。反映氧化物膜中的应力状况。P-B比在l～2之间的金属，其表面氧化物膜中产生一定程度的压应力，膜比较致密，金属抗氧化性强。P-B比小于1或大于2时，氧化物膜中产生张应力或过大的压应力，容易造成膜破裂，金属抗氧化性低。
CAS号：
性质：金属与氧结合在金属表面生成的氧化物膜中的每个金属离子体积与金属中的每个金属原子体积之比。反映氧化物膜中的应力状况。P-B比在l～2之间的金属，其表面氧化物膜中产生一定程度的压应力，膜比较致密，金属抗氧化性强。P-B比小于1或大于2时，氧化物膜中产生张应力或过大的压应力，容易造成膜破裂，金属抗氧化性低。