1) Tosyl cellulose sulfate sodium
甲苯磺酰纤维素硫酸盐
1.
Tosyl cellulose sulfate sodium and chitosan ultra thin films were self assembled through electrostatic attraction on the positively charged quartz substrate.
本文将纤维素的一种新型离子型衍生物——甲苯磺酰纤维素硫酸盐 ,在处理过的石英基片和硅基片上自组装成膜 ,并在其上再自组装一层脱乙酰壳聚糖膜 。
2) cellulose tosylate
纤维素甲苯磺酸酯
1.
The first is the tosylation of cellulose with tosylchloride using triethylamine as catalyst and the dimethylacetamide/LiCl system as solvent to obtain cellulose tosylate with certain ester number.
首先利用棉纤维素粉溶解在DMAc/LiCl溶剂体系中,与甲苯磺酰氯进行均相磺酰化,得到一定酯化度的纤维素甲苯磺酸酯,然后在DMSO中进行均相亲核叠氮反应,得到取代度为0。
3) sulfite cellulose
亚硫酸盐纤维素
4) cellulose sulphate, sodium salt of
硫酸纤维素钠盐
5) Sulfurous acid, monosodium salt, reaction products with formaldehyde, sulfonylbis[phenol] and urea, sodium salts
亚硫酸单钠盐与甲醛、磺酰基双[苯酚]和尿素的反应产物钠盐
6) polystyrylsulfonylhydrazinecarbodithioic acid resin
聚苯乙烯磺酰肼基二硫代甲酸盐树脂
1.
A colorimetric analytical method was established for the determination of degree of functionalization of the salt of polystyrylsulfonylhydrazinecarbodithioic acid resin prepared from polystyrene beads.
以此方法测定了用交联度和颗粒度不同的两种聚苯乙烯白球在相同条件下合成的聚苯乙烯磺酰肼基二硫代甲酸盐树脂的功能化程度,分别为1。
补充资料：4-甲苯磺酰肼
分子式：C7H10N2O2S
分子量：186.23
CAS号：1576-35-8
性质：白色结晶粉末。熔点108-110℃（分解）。易溶于碱，溶于甲醇、乙醇和丁酮，微溶于水、醛类，不溶于苯、甲苯。加热到105℃以上逐渐由熔融状态进行分解，放出氮气，标准发气量120ml/g，在热水中水解产生磺酸，分解出氮气，常温下无吸湿潮解现象，化学性质较稳定。
制备方法：对甲苯磺酰氯与水合肼在苯介质中于60-70℃进行缩合，排放的氯化氢用水吸收。过滤，水洗，于65℃干燥得发泡剂TSH。滤液中的苯层供循环使用，水层可回收硫酸肼。原料消耗（kg/t）对甲苯磺酰氯（96.8%） 1110水合肼（40%） 820苯 520
用途：用作天然橡胶、合成橡胶及多种塑料的发泡剂，使塑料及橡胶制品产生细微闭孔结构，制品的收缩率小，抗撕裂强度大。
分子量：186.23
CAS号：1576-35-8
性质：白色结晶粉末。熔点108-110℃（分解）。易溶于碱，溶于甲醇、乙醇和丁酮，微溶于水、醛类，不溶于苯、甲苯。加热到105℃以上逐渐由熔融状态进行分解，放出氮气，标准发气量120ml/g，在热水中水解产生磺酸，分解出氮气，常温下无吸湿潮解现象，化学性质较稳定。
制备方法：对甲苯磺酰氯与水合肼在苯介质中于60-70℃进行缩合，排放的氯化氢用水吸收。过滤，水洗，于65℃干燥得发泡剂TSH。滤液中的苯层供循环使用，水层可回收硫酸肼。原料消耗（kg/t）对甲苯磺酰氯（96.8%） 1110水合肼（40%） 820苯 520
用途：用作天然橡胶、合成橡胶及多种塑料的发泡剂，使塑料及橡胶制品产生细微闭孔结构，制品的收缩率小，抗撕裂强度大。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。