1) Ti-bearing steel
含钛钢
2) titanium steel
含钛钢
3) titanium material
含钛料
1.
It could be used in microwave leaching course to remove impurities such as Ca and Mg for preparing rich titanium material from titanium material.
研究了一种新型的改性剂,可以将其应用于微波加热含钛料除钙镁等杂质制取高品质富钛料的浸出过程,并进行了系统的条件实验。
4) titania slag
含钛渣
1.
For titania slag the relationship between viscosity and temperature as well as conductivity and time was investigated.
研究了含钛渣的粘度、电导率与温度、渣成分、时间的关系,获得了渣中初始结晶相CaTiO3结晶过程的动力学参数,建立了CaTiO3相的结晶温度与渣碱度之间的关系式。
5) Ti-containing mineral
含钛矿物
1.
An investigation is made of the reaction kinetics of Ti-containing minerals using diasporic bauxite as raw material according to the principle of the equal-reaction efficiency method.
以中国某矿区的一水硬铝石型铝土矿为原料,采用等溶出率方法的原理,进行了含钛矿物反应动力学的研究。
6) TiO2 content
含钛量
1.
Slag cement is prepared by using slag (with different TiO2 content),clinker and gypsum (with various quantity).
采用不同含钛量的矿渣与水泥熟料及不同掺量的石膏配制成矿渣水泥,通过分析混合水泥中石膏掺量与矿渣掺量及矿渣中TiO2含量的关系,研究了矿渣水泥中矿渣含钛量与石膏掺量的关系。
参考词条
补充资料：含钛钢
分子式：
CAS号：
性质： 含有一定量钛的钢。钛和碳、氮、氧都有极强的亲和力，钛在钢中主要以碳化物的形态存在，它是良好的脱氧去气剂及固定碳、氮的有效元素。钛可细化钢的组织和晶粒，并能提高晶粒粗化温度至1000℃以上。由于钛和碳之间的亲和力大于铬与碳，故用来消除不锈钢的晶间腐蚀。钛是强铁素体形成元素，强烈提高A1及A3。固溶的钛可提高淬透性，也可强化铁素体。钛在钢中的含量很低，当钛>0.025%时即认为是合金元素。
CAS号：
性质： 含有一定量钛的钢。钛和碳、氮、氧都有极强的亲和力，钛在钢中主要以碳化物的形态存在，它是良好的脱氧去气剂及固定碳、氮的有效元素。钛可细化钢的组织和晶粒，并能提高晶粒粗化温度至1000℃以上。由于钛和碳之间的亲和力大于铬与碳，故用来消除不锈钢的晶间腐蚀。钛是强铁素体形成元素，强烈提高A1及A3。固溶的钛可提高淬透性，也可强化铁素体。钛在钢中的含量很低，当钛>0.025%时即认为是合金元素。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。