1) aluminium oxide
铝胶
2) alumina sol
铝胶
1.
A wet chemical method was cidopted to introduce alumina sol to surface-modification of alumina bubble and in-situ decomposition characteristics, distribution of alumina sol, mi-crostructure and mechanical properties of surface-modified alumina bubble were studied by SEM, XRD, Coulter LS Particle Size Analyzer and self-preparation experimental device for measurement of compressive resistance.
采用湿化学的方式引入铝胶对氧化铝空心球进行表面修饰改性;采用SEM、XRD、激光粒度仪和自制耐压装置研究铝胶分解特性、分布状态、氧化铝空心球表面改性前后显微结构及力学强度变化。
3) silica-alumina gel
硅铝胶
1.
In this study,zeolite catalysts,in which HY zeolite was used as active component and alumina gel,silica-alumina gel and titania-alumina gel as binders,were prepared for removal of trace olefin in aromatics.
本研究以铝胶、硅铝胶及钛铝胶为粘合剂,以HY分子筛为主要活性组分制备了芳烃脱烯烃分子筛催化剂。
4) alumina-washcoating
铝胶涂层
1.
The properties of calcined alumina-washcoating, such as specific surface areas and structure was investigated and measured by BET and XRD.
结果表明：铝胶涂层具有一定的比表面积，负载量随着铝胶密度的增加而增加。
5) aluminum phosphate colloid
磷酸铝胶
6) magnesia-alumina colloid
镁铝胶
参考词条
补充资料：铝胶
Al2O3 分子量101.96
白色或微红色棒状物。密度3．5-3．9g／cm3。熔点2045℃。沸点2980℃。比表面积200-400m2／g。不溶于水，微溶于碱或酸。其水合物有一水物和三水物两种，并各具有α和γ两种变体，将水合物在200～600℃温度下加热可生成不同晶形的活性氧化铝。实际应用令多以γ型活性氧化铝为主。
应用领域 用于多种气体和液体如空气、氧气、氢气、天然气、甲烷、氟利昂、氨、氯化氢、硫化氢、二氧化硫等的干燥。石油和化学工业上用作许多化学反应过程中的吸附剂、催化剂及其载体。另外，还用作变压器油和透平油的脱酸剂，以及用于色层分析中。
白色或微红色棒状物。密度3．5-3．9g／cm3。熔点2045℃。沸点2980℃。比表面积200-400m2／g。不溶于水，微溶于碱或酸。其水合物有一水物和三水物两种，并各具有α和γ两种变体，将水合物在200～600℃温度下加热可生成不同晶形的活性氧化铝。实际应用令多以γ型活性氧化铝为主。
应用领域 用于多种气体和液体如空气、氧气、氢气、天然气、甲烷、氟利昂、氨、氯化氢、硫化氢、二氧化硫等的干燥。石油和化学工业上用作许多化学反应过程中的吸附剂、催化剂及其载体。另外，还用作变压器油和透平油的脱酸剂，以及用于色层分析中。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。