1) FGH95 powders
FGH95粉末
1.
The dendrite microsegregations in PREP FGH95 powders has been studied by using SEM The results show that there are riched with Mo,Ti,Ni elements,and poored with Ni, Co,W elements between the powders dendrite arm It also seems that the dendrite microsegregations decrease with decreasing particle size Compared with argon atomized powders, the dendrite microsegregations in PREP FGH95 powders is lowe
测定两种工艺方法生产的 FGH95粉末颗粒截面的枝晶偏析和胞晶偏析。
2) FGH95 alloy powder
FGH95合金粉末
1.
Non-equilibrium solute partition of rapidly solidified FGH95 alloy powder;
快速凝固FGH95合金粉末的非平衡溶质分配
2.
Analysis of efficient during water elutriation process of separating ceramic inclusions from FGH95 alloy powder;
分离FGH95合金粉末中陶瓷夹杂物的水淘析法有效性分析
3.
The results indicate that the geometry integrity of metastable MC type carbide in rapidly solidified FGH95 alloy powders changed from regular morphology .
结果表明:快速凝固FGH95合金粉末中亚稳MC型碳化物形态的几何完整度随粉末颗粒尺寸减小由规则形态向复杂形态变化,不同尺寸粉末颗粒中碳化物的形态和数量决定于凝固过程中热学参数的变化和非平衡溶质分配系数的不同。
3) FGH95 P/M material
FGH95粉末材料
4) FGH95 powder nickel-base superalloy
FGH95粉末镍基合金
1.
By means of the measurement of creep curves and microstructure observation,an investigation has been made into the creep behaviors and deformation features of FGH95 powder nickel-base superalloy.
通过蠕变曲线的测定及组织形貌的观察,研究了FGH95粉末镍基合金的蠕变行为及变形特征。
2.
By means of the measurement of creep curves and microstructure observation,an investigation has been made into the microstructure and creep behaviors of FGH95 powder nickel-base superalloy.
通过进行蠕变曲线测定和组织形貌观察,研究了FGH95粉末镍基合金的微观组织结构与蠕变行为。
5) FGH95 superalloy powders
FGH95高温合金粉末
1.
Carbide and its stability in FGH95 superalloy powders during rapid solidification;
对快速凝固FGH95高温合金粉末中的碳化物及其稳定性进行实验研究,分析了粉末颗粒凝固过程中的热学参数和非平衡溶质分配对碳化物形成过程的影响。
6) FGH95 superalloy powder
FGH95高温合金粉末
1.
Pre-heat treatment of PREP FGH95 superalloy powders;
等离子旋转电极雾化FGH95高温合金粉末的预热处理
2.
The microstructure characteristics of FGH95 superalloy powders prepared by plasma rotating electrode processing (PREP) have been investigated by using SEM.
对等离子旋转电极雾化(PREP)FGH95高温合金粉末颗粒凝固组织特征进行研究,并用数值分析方法计算了FGH95合金粉末凝固过程中冷却速率与粉末粒度之间的关系,结果表明:粉末颗粒表面凝固组织主要是树枝晶和胞状长大晶,随着粉末颗粒尺寸的减小,内部凝固组织由树枝晶为主逐渐转变为以胞状晶及微晶组织为主,冷却速率与粉末粒度之间的关系为T=2。
3.
In order to investigate the relation between microstructure of superalloy powders and the heat treatment system, this paper studied the transformation of carbides in FGH95 superalloy powders prepared by plasma rotating electrode processing (PREP) under different pre-heating treatment temperature.
对等离子旋转电极雾化(PREP)FGH95高温合金粉末颗粒在不同温度下进行预热处理,并对热处理粉末中碳化物的变化规律进行分析,结果表明:经预热处理,粉末颗粒中的MC’型亚稳碳化物发生分解和转变,析出稳定的MC,M_(23)C_6及M_6C型碳化物,明显改变碳化物的稳定性和分布状态。
补充资料：Aizen Cathilon Pink FGH
分子式：C22H26Cl2N2
分子量：398.35
CAS号：3648-36-0
性质：暗红色均匀粉状物。配伍值4。属半菁阳离子染料。溶于水呈鲜明桃红色，在硫酸中呈黄色，稀释后转红光橙色。
制备方法：以N-甲基苯胺，环氧乙烷，三氯氧磷，二甲基甲酰胺和1,3,3-三甲基-2-亚甲基吲哚啉为基本原料。先由N-甲基苯胺用环氧乙烷进行羟乙基化，再用三氯氧磷进行氯化，用二甲基甲酰胺醛化，而后与1,3,3-三甲基-2-亚甲基吲哚啉缩合，最后过滤、干燥即得成品。原料消耗(kg/t)磷酸 224 亚硫酸氢钠 580乙醇 440 锌粉 9氯磺酸 3560 硫酸 360苯 750 甲乙酮 152甲醇 930 氨水（25%） 680氢氧化钠（100%） 430 N-甲基苯胺 178苯胺 260 二甲基甲酰胺（DMF） 190盐酸（31%） 1200 三氯氧磷 550亚硝酸钠190环氧乙烷80
用途：用于腈纶及其混纺织物的染色和印花。还可用于乙酸纤维和聚氯乙烯纤维的染色。
分子量：398.35
CAS号：3648-36-0
性质：暗红色均匀粉状物。配伍值4。属半菁阳离子染料。溶于水呈鲜明桃红色，在硫酸中呈黄色，稀释后转红光橙色。
制备方法：以N-甲基苯胺，环氧乙烷，三氯氧磷，二甲基甲酰胺和1,3,3-三甲基-2-亚甲基吲哚啉为基本原料。先由N-甲基苯胺用环氧乙烷进行羟乙基化，再用三氯氧磷进行氯化，用二甲基甲酰胺醛化，而后与1,3,3-三甲基-2-亚甲基吲哚啉缩合，最后过滤、干燥即得成品。原料消耗(kg/t)磷酸 224 亚硫酸氢钠 580乙醇 440 锌粉 9氯磺酸 3560 硫酸 360苯 750 甲乙酮 152甲醇 930 氨水（25%） 680氢氧化钠（100%） 430 N-甲基苯胺 178苯胺 260 二甲基甲酰胺（DMF） 190盐酸（31%） 1200 三氯氧磷 550亚硝酸钠190环氧乙烷80
用途：用于腈纶及其混纺织物的染色和印花。还可用于乙酸纤维和聚氯乙烯纤维的染色。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条