1) O2-Br2-Ar atmosphere
氧-溴-氩气氛
2) Ar-O_2 controlled atmosphere
氩氧控制气氛
1.
A method for determination of hafnium in zirconium under Ar-O_2 controlled atmosphere was developed and the conditions of ratio of Ar-O_2, excited current and exposed time were optimized.
研究了在氩氧控制气氛条件下锆中铪的分析条件,对氩氧比、激发电流、曝光时间等实验参数进行了选择。
3) Ar atmosphere
氩(Ar)气氛
1.
The results show that the buckytubes are prepared by using Ar atmosphere better than using He atmosphere in carbon arc method.
用氦（He）气氛和用氩（Ar）气氛的制各工艺条件、阴极沉积物的生长速率、布基管产率与惰性气体压强的关系。
4) in vacuum
氩气氛
1.
3kPa), the sample starts to decompose at about 700～790℃ ; in vacuum (10 -2 ～10 -3 Pa),the sample starts to change at about 300℃, and shows a thermal instability.
结果表明：压力对样品的分解影响很大，在氩气氛中（１０１。
5) argon cell
氩气氛小室
6) argon atmosphere annealing
氩气氛退火
1.
Thermal infrared detecting VO2 film has been prepared by radio frequency megnetron sputtering deposition and argon atmosphere annealing.
采用射频磁控溅射沉积方法,结合氩气氛退火工艺制备了热红外探测VO2薄膜,通过优化工艺,制备出化学计量比接近理论值、高质量的VO2薄膜。
补充资料：氩39-氩40法测年
分子式：
CAS号：
性质：将含钾样品放入核反应堆中接受快中子照射，40K核被打进一个中子，而后放出一个质子，形成39Ar，用质谱计测定被照射样品的40Ar/39Ar比值，代替常规钾-氩法中40Ar/40K比值，从而计算出样品年龄的方法，计算公式如下：t=λ-1ln(1+J•40Ar/39Ar)。式中J=39Ar/40Ar•λ/λkΔT∫φ(ε)σ(ε)dε是样品照射持续的时间，Ф(ε)是能量为ε时的中子通量，σ(ε)为39K(n，p)39Ar的反应截面，实验中用一已知年龄(ts)的标准与待测样品一块进行辐照，由下式求得J值：J=(eλt-1)/(40Ar/39Ar)。此方法解决了过去钾、氩分别由不同方法测定所产生的不同误差使年龄精度较低的弊端；同时由于照射后样品氩的释放可采用阶段加温方法，对一个样品便可获得一系列的表面年龄，最终得到代表矿物或岩石结晶的稳定坪年龄；或由等时线法处理得到样品的年龄、认识外来氩的混入状况。
CAS号：
性质：将含钾样品放入核反应堆中接受快中子照射，40K核被打进一个中子，而后放出一个质子，形成39Ar，用质谱计测定被照射样品的40Ar/39Ar比值，代替常规钾-氩法中40Ar/40K比值，从而计算出样品年龄的方法，计算公式如下：t=λ-1ln(1+J•40Ar/39Ar)。式中J=39Ar/40Ar•λ/λkΔT∫φ(ε)σ(ε)dε是样品照射持续的时间，Ф(ε)是能量为ε时的中子通量，σ(ε)为39K(n，p)39Ar的反应截面，实验中用一已知年龄(ts)的标准与待测样品一块进行辐照，由下式求得J值：J=(eλt-1)/(40Ar/39Ar)。此方法解决了过去钾、氩分别由不同方法测定所产生的不同误差使年龄精度较低的弊端；同时由于照射后样品氩的释放可采用阶段加温方法，对一个样品便可获得一系列的表面年龄，最终得到代表矿物或岩石结晶的稳定坪年龄；或由等时线法处理得到样品的年龄、认识外来氩的混入状况。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条