1) Mo single crystal
钼单晶
1.
A sample of Mo single crystal has been identified, and the orientation deviation angle of (111) plane has been measured.
采用X射线θ扫描旋转法和金相分析相结合的方法 ,对区熔法生长的钼单晶样品进行了判定和 ( 111)晶面取向偏离角的测试 ,对钼单晶中的小角晶界进行了观察和分析。
2) Monocrystal molybdenum
钼单晶体
1.
Monocrystal molybdenum is a kind of widely used and important refractory metal.
利用籽晶法电子束悬浮区熔技术成功制备了晶体取向为(111)的钼单晶体,采用多种分析测试手段,研究了区熔速率对钼单晶体质量的影响。
3) lead molybdate single crystal
钼酸铅单晶
4) molybdenum-niobium single crystal
钼-铌合金单晶
5) Mo-Nb alloy single crystal
钼铌合金单晶
1.
The influences of vacuum(or residual pressure) in the melting chamber,chemical composition of Mo-Nb alloy feedstock bars,growing rate and rotation rate on processing Mo-Nb alloy single crystal are investigated.
研究熔炼室真空度、合金原料棒化学成分、熔炼速度、搅拌速度等对钼铌合金单晶制备的影响。
6) poly-crystal Mo
多晶钼
1.
Our experiments showed that it can ensure the same specific property of thermal emission current by use of poly-crystal Mo insteal of single-crystal Mo.
2× 10 - 6 Pa的真空下 ,对多晶钼尖端阴极的热发射特性进行了实验研究 ,在工作温度 1。