1) Zero Non-Metallic Inclusion Steel
零非金属夹杂钢
1.
Super Clean Steels and Zero Non-Metallic Inclusion Steels;
超洁净钢和零非金属夹杂钢
4) non-metallic inclusion
非金属夹杂
1.
Effect of Non-Metallic Inclusion on Corrosion Resistance of Steel 35CrMo for Natural Gas Well;
非金属夹杂物对天然气油井用35CrMo钢耐蚀性的影响
2.
SEM observation indicated that the fatigue crack mostly initiated at the surface or subsurface for the samples failed in the regime of 5×10~6—10~8 cyc,and at the internal non-metallic inclusion for the.
SEM断口观察表明,在5×10~6—10~8cyc范围内,疲劳裂纹基本上萌生于试样表面或亚表面,而在10~8—10~9cyc范围内,疲劳裂纹主要萌生于试样内部的非金属夹杂物。
3.
The results showed that the major cause of reducing diameter was more non-metallic inclusion in the steel than standard value,billet segregation and shrinkage void.
用扫描电镜、大型金相显微镜观察分析高碳钢盘条的缩径,结果表明:造成缩径的主要原因是盘条中的非金属夹杂物超标、方坯偏析和缩孔。
5) non-metallic inclusions
非金属夹杂
1.
They include stabilizing molten steel compositions and decreasing non-metallic inclusions in steel so as to improve both surface and internal quality.
介绍了武钢第一炼钢厂通过稳定钢水成分,降低钢中非金属夹杂来改善SWRH82B方坯的表面质量和内部质量,以满足用户要求的情况。
2.
The forecast model for existing situation of non-metallic inclusions in continuous cast slab is established through combining the study method provided by other researchers with the investigating result of non-metallic inclusions in continuous cast slab at PZH Steel.
参考有关研究提供的方法 ,结合攀钢铸机条件及非金属夹杂检测结果 ,建立了攀钢板坯的非金属夹杂存在预报模型。
3.
These non-metallic inclusions badly dispersed in the alloy steel are harmful to the mechanical properties of welded joints.
结果表明:中小线性能量焊接,层间温度在80℃～200℃变化时,焊接接头-30℃冲击韧性好;线能量超过40kJ/cm时,焊接接头冲击韧性明显下降;其中存在大量的硫化物,这些非金属夹杂物数量多,分布极不平均,导致焊接接头低温冲击韧性值离散度大,数值偏低。
6) inclusion
[英][ɪn'klu:ʒn] [美][ɪn'kluʒən]
非金属夹杂
1.
The effects of processing variables which contain the frequency of magnetic field, magnetic flux density, imposed time, the diameter of inclusions on the efficiency of inclusion separation in aluminum melt with high frequency magnetic field were experimentally investigated.
对利用高频磁场分离静置Ａｌ熔体中非金属夹杂的工艺参数进行了研究。
2.
A series of measurements including macrograph, inclusion, segregation and property of rolled steel products confirm that the contionus casting process gives satisfaction to the quality of the products.
内容包括:铸坯的低倍组织,非金属夹杂物、成分偏析及钢材性能。
补充资料：非金属夹杂
非金属夹杂
non-metallic inclusion
fejjinshu Jjoza非金属夹杂(non一metalli。inelusion)金属中含有的非成分和性能所要求的非金属相。非金属夹杂来源于金属熔炼和铸造过程中，熔体中各元素与炉气等介质反应产生的氧化物和氮化物以及由炉体、炉衬、罐衬、汤道、水口、中间罐和炉料等带入的耐火材料残渣、灰分、脱氧产物和残留熔剂等。钢中常见的非金属夹杂有氧化物(A12O3、Mn02、Feo、Fe3O;和Fe20:等)、硫化物(FeS、MnS、MnS·FeS等)、硅酸盐[(如硅酸亚铁(ZFeO·5102)、硅酸亚锰(ZMnO·510:)和铁锰硅酸盐(mFeo·nMnO·PSIO。等)j和氮化物一(TIN、ZrN)等。铜及铜合金中的非金属夹杂常有CuZO、CuO、CuZS、CuS等。铝及铝合金中有A12O3、MgO、5102、A12O:·MgO(尖晶石)，还有一些净化处理时产生的氯化物(M邪12)和氮化物等。镁及镁合金中主要夹杂物是M扣、少量的Mg3N:和MgZe。钦及钦合金中的夹杂为Tio、TIOZ、TiZO3、TiaOS和TIN等。 不同形态的夹杂物混杂在金属内部，破坏了金属的连续性和完整性。夹杂物同金属之间的结合情况不同、弹性和塑性的不同以及热膨胀系数的差异，常使金属材料的塑性、韧性、强度、疲劳极限和耐蚀性等受到显著影响，同时也常常影响加工零件的表面质量和加工工具的寿命。非金属夹杂分塑性夹杂和脆性夹杂。塑性夹杂如MnS等随金属变形而延伸轧薄。脆性夹杂如Al:0。等随金属变形而破碎。另一些夹杂物软化点及硬度很高，热加工中不变形，不破碎，保持原来形状，如TIN、稀土硫氧化物等。铜中氧化夹杂CuZO常分布在晶界上，Cu20是一种硬脆相，会降低金属的热塑性，还影响铜的导电能力。因此，导体铜最好是无氧铜(含氧量在。:003%以下)。铝合金在熔炼过程中，熔体表面的氧化皮膜很容易混进熔体进入铸锭形成夹杂物。这些氧化膜在金属的塑性变形过程中会使金属产生分层。特别是在棋锻件中，氧化膜沿金属流线分布会严重影响锻件的疲劳性能。因此，飞行器锻件对氧化膜有非常严格的要求。 非金属夹杂的形态、大小和在金属中分布的情况不同，对金属性能有不同的影响。通常集中分布、尺寸较大的颗粒和团块对金属材料性能的影响最大;分散、细小颗粒的影响相对要小一些。高度弥散分布的杂质可作为异质晶核使铸锭晶粒细化，在变形和热处理过程中影响晶界迁移，可改善再结晶组织。非金属夹杂物按占母体金属的质量百分数评定，或根据产品标准中的图片评级，并按产品的使用要求确定允许存在的百分比或级别。钢轨中的非金属夹杂如图所示。髓 钢轨中的非金属夹杂 防止非金属夹杂的措施有:熔体炉内净化、悠体炉外净化、吹氢搅拌、保护浇注、控温浇注等。 (崔峰许庆泰马宏声)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。