1) thermal expansion stress
热膨胀应力
1.
Analysis of the FEM for thermal expansion stress of BOF vessel;
BOF炉体热膨胀应力的有限元分析
2.
,when the thickness of asbestos board is about 30 mm, the shell temperature can be controlled within 360℃ , the thermal expansion stress of the shell is only 50 % of those without asbestos board, and this can help reduce the creep deformation rate of .
对中小型转炉提出了加隔热层石棉板降低炉壳表面温度的方法,并对重钢80t转炉炉身段进行了温度场及热应力分析,结果表明:当石棉板的厚度为30mm左右时,炉壳温度就能控制在360℃以内,炉壳所受到的热膨胀应力仅为没加石棉板时的50%,有利于降低炉壳的蠕变变形速率。
2) heat swelling power
热膨胀力
1.
The change laws of heat swelling power and porosity of sandstone and limestone were researched at different temperatures using a heat swelling power experimental system and a porosity test apparatus.
采用热膨胀力测试系统和孔隙测定装置研究了不同温度条件下砂岩和石灰岩的热膨胀力和孔隙率的变化规律。
3) swelling stress
膨胀应力
1.
Relation between effective stress and swelling stress of coal body;
煤体有效应力与膨胀应力之间关系的分析
2.
Experimental research on the swelling stress of limestone in the second coal mine of Tian'an,Pingdingshan city
平顶山天安二矿石灰岩膨胀应力的试验研究
3.
The characteristic graph of soft rock linear swelling ratio and swelling stress and final water saturation ratio ,and related analysis results of the ratio about mud rock dry saturated absorbed water ratio and the quality contained montmorillobnite are obtained based on a large number swelling experimental results about soft rock are got.
主要研究膨胀岩的膨胀特性,用软岩膨胀测定仪对重塑试件和原岩试件进行软岩膨胀率的测定,根据大量的软岩膨胀性试验成果,找出了软岩膨胀应力与线膨胀率、线膨胀最终饱和含水率特性曲线,泥质岩干燥饱和吸水率与蒙脱石含量特性曲线的相关分析结果,采用风干或烘干的不规则试件吸水率的大小作为对膨胀岩的判别和评价的依据。
4) expansive stress
膨胀应力
1.
The parameters include the mixing ratio of expansive agent,the expansive diameter,the distance between water injection holes and the test of the expansive stress.
全长膨胀塑料锚杆作为一种新型的巷帮支护材料 ,其性能参数严重影响着它在工程中的实际应用 ,为此 ,作者对其性能参数进行了实验室测定 ,主要包括 :膨胀剂配比、自由膨胀直径、注水孔间距和膨胀应力 。
2.
One is the expansive stress analysis.
膨胀应力法：定量分析混凝土中残存的ｆＣａＯ，估测ｆＣａＯ水化产生的膨胀应力，比较膨胀应力与混凝土抗拉强度的大小，据此评定混凝土体积安定性；沸煮法：根据沸煮前后混凝土超声波声速、劈裂抗拉强度及混凝土薄切片的变化，评定混凝土体积安定性。
5) expanding stress
膨胀应力
1.
In view of cracks appeared in the connecting point of post shoulder and beam for workshop steel-pipe concrete post in some steel rolling plant,the reason and the expanding cause of vertical cracks in aspect of forming of water-sulphur-calcium aluminate are analyzed,accompanying with expanding stress in concrete,and welding seams design and construction.
针对某热轧带钢厂钢卷库厂房钢管混凝土柱肩梁部出现开裂的情况,从混凝土内部形成水化硫铝酸钙伴生膨胀应力,以及焊缝设计、施工存在的问题,分析了竖向裂缝的成因及扩展,进而提出了此类缺陷的预防措施及采取加劲肋、环向圈等,使结构恢复正常使用的加固技措。
6) thermal expansion effect
热膨胀效应
补充资料：材料热膨胀
材料热膨胀
thermal expansion of material
材料热膨胀比ermal expansion of material材料在一定的压力下，因温度变化而表现出尺寸变化的现象。在研究单摆的时间测量过程中，荷兰P.van穆申布鲁克(Musschenbrock)在1730年测量了几种用于单摆的金属材料的热膨胀。 为了对材料的热膨胀进行定量描述，定义了热膨胀系数。 _1，口V、_Qv一~补，、飞万万少尸二常致 犷份l式中av为体膨胀系数，V为体积，T为温度，尸为压力。对于线性或单向情况: _1，弘、山-一了一又-不万布夕尸=常数 JJ 01式中。为线膨胀系数，L为长度。热膨胀系数是一个二阶对称张量:Ql山吼兔处嘶飞兔飞式中a1，处，兔描述体积变化;山，兔，瀚描述形状变化。对于具有不同对称性的材料，这几个系数的情况不同，对各向同性材料价=a2二伪，其余3项为零。 当固体处于德拜温度以下时，a随温度变化很快。温度高于德拜温度时，Q近似于常数。一般材料在室温时，一有如下近似关系 Z二几〔1·十。(t一拓)〕民七中而为温度而时的长度，l为温度为t时的长度。 对于热膨胀系签玫的侧量方法的研究，开始于18世纪。主要方法为:(习力学方法，如顶杆法;②电学方法，如电容法、电撼专法;③光学方法，如干射法，衍射法;④X射线衍射余专。目前对线膨胀的测量灵敏度可达10一13。 关于固体热膨胀的微观理论，与晶格振动理论的发展密切相关。固体内原子的线性谐振不能引起体积的变化。热膨胀是由于热激发振动的非线性引起的。E.格临爱森(Gruneisen)生良早对热膨胀的理论进行了系统研究，他引户、了准简谐振动模型，指出膨胀系数和固体的定容比热成正比。在」低温下(小振幅振动)膨胀系数趋近于零。除了晶格非诣‘振动外，材料的电、磁作用，缺陷、相变等都与热膨上长性质有密切关系。所以对热膨胀的测量极大地增长了弓戈们对以上各领域的知识。 以上主要介绍了卜团体材料的热膨胀，对于气体及液体，其分子作用机制2乏数据表现的方式都与固体不同。 对于理想气体有 尸VR T一G式中尸为绝对压力，飞/为比体积，T为绝对温度，R为理想气体常数，‘为分子重量。体膨胀系数 1，口V、街=万7、石万布夕尸=常数 y门J工对理想气体av为l/T。真实气体由范德瓦耳斯(Vander Waals)方程描述。 对于液体，沂是压力和温度的函数。尽管Qv通常在大温度范围内被认为是常数(如液体膨胀温度计)，但有些变化需要考虑，如水在温度由oaC到4oC变化时收缩而在此之上膨胀。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。