1) unsaturated glycidyl ether
不饱和缩水甘油醚
1.
The epoxy modified water soluble silicone fluid was obtained by the hydrosilylation reaction of low H containing silicone fluid with unsaturated glycidyl ether and polyoxyethylene diallyl oxide under the catalysis of chloroplatinic acid.
在氯铂酸催化下 ,通过低含氢硅油与不饱和缩水甘油醚、聚氧乙烯烯丙醚的硅氢加成反应 ,制得环氧改性水溶性硅油 ;采用化学滴定法测定未反应活性氢的质量分数 ,从而确定含氢硅油的转化率 ;在合成过程中采用甲苯作溶剂、正丙醇作封闭剂 ,可避免在中和反应后发生交联 ,有利于保证产品的稳定性。
2) Fatty acids, C18-unsatd., dimers, reaction products with formaldehyde-phenol polymer glycidyl ether
C18不饱和脂肪酸二聚体与甲醛-苯酚聚合物缩水甘油醚的反应产物
3) unsaturated polyester resin of acrylic glycidic ester type
丙烯酸缩水甘油酯型不饱和聚酯树脂
4) glycidyl ether
缩水甘油醚
1.
Study on catalytic synthesis and synthetic process of mixed alcohol glycidyl ether;
混合醇缩水甘油醚的催化合成及其工艺研究
2.
Using phenyl glycidyl ether(1),2-methylphenyl glycidyl ether(2),benzyl glycidyl ether(3)andβ-cyclodextrin as raw materials,in 1.
以苯基缩水甘油醚、邻甲基酚缩水甘油醚及苯甲基缩水甘油醚(1～3)和β-环糊精为原料,分别在弱碱水溶液(1。
3.
Four intermediates of glycidyl ethers,namely ethyl glycidyl ether(1),propyl glycidyl ether(2),butyl glycidyl ether(3)and amyl glycidyl ether(4),were obtained through a phase-transfer catalytic meth-odology using acyclic alcohol and epichlorohydrin as raw materials.
以环氧氯丙烷和脂肪醇为原料,通过相转移催化法合成了乙基、正丙基、正丁基和正戊基缩水甘油醚(1～4),并利用所合成的缩水甘油醚和β-环糊精为原料,分别在弱碱水溶液(1。
5) Diglycidyl ether
缩水甘油醚
1.
In this paper,the synthetic technics of a novel epoxide diluent-cylohexanediol-1,2 diglycidyl ether was sdudied by othogonal method.
通过正交实验对1,2-环己二醇二缩水甘油醚的合成工艺进行了研究,考察了原料配比、催化剂量、醚化温度、闭环温度等因素对实验的影响。
2.
The optimal conditions of synthesis of tetraromobisphenol-A based diglycidyl ether is obtained by studying the influences of temperature, type of alkali addition, quantity of alkali added on the reaction.
通过探索温度、加碱方式、碱用量等因素对合成四溴双酚A二缩水甘油醚的影响 ,优化出较好的合成条件。
3.
Different molecular weight polymer--polyethylene glycol diglycidyl ether(PEGO) were synthesized and structures of them were characterized by 1H-NMR, IR.
合成了不同分子量的聚乙二醇缩水甘油醚 (PEGO) ,用 1H- NMR、红外吸收光谱对其进行了表征 ,并将其用于改性丝素膜。
6) glycidol ether
缩水甘油醚
1.
Some glycidol ether monomer(GE) were prepared by reacting epichlorohydrin(ECH) with phenol and/or alcohol; α allyl glycidol ether, β chloroethyl glycidol ether, benzene glycidol ether, m tolyl glycidol ether, benzyl glycidol ether.
以醇和酚与环氧氯丙烷 (ECH)反应合成了 α-烯丙基缩水甘油醚、β-氯乙基缩水甘油醚、苯基缩水甘油醚、间甲苯缩水甘油醚、苄基缩水甘油醚等单体 。
2.
Because of the existence of long-chain additive glycidol ether epoxy resin.
由于以长链线型缩水甘油醚环氧树脂做活性增韧剂，和其它组份一道配制而成了具有透明度高，柔韧性、回弹性及粘接性均好的粘合剂，可适用于光学塑料，铭牌商标、立体水晶化装饰及要求具有柔韧性的场合。
补充资料：甘油二缩水甘油醚
CAS：60453-84-1
中文名称：2-丙烯酸-(2-羟基-1,3-亚丙基)二[氧基(2-羟基-3,1-亚丙基)]酯；甘油二缩水甘油醚； 丙烯酸的加合物
英文名称：Glycerine diglycidyl ether acrylic acid adducts；glycerol 1,3-diglycerolate diacrylate
中文名称：2-丙烯酸-(2-羟基-1,3-亚丙基)二[氧基(2-羟基-3,1-亚丙基)]酯；甘油二缩水甘油醚； 丙烯酸的加合物
英文名称：Glycerine diglycidyl ether acrylic acid adducts；glycerol 1,3-diglycerolate diacrylate