1) γ-isocyanatepropyltriethoxy silane
γ-异氰酸酯丙基三乙氧基硅烷
2) IPTES
γ-异氰酸酯基丙基三乙氧基硅烷
1.
γ-isocyanatopropyltriethoxysilane(IPTES)was grafted successfully on fundamental chain epoxy resin in order to improve water resistance of epoxy/ polyamide(EP/PAI)resin system.
为了提高环氧/聚酰胺(EP/PAI)树脂体系的耐水性,在环氧树脂的主链上成功地接枝了γ-异氰酸酯基丙基三乙氧基硅烷(IPTES)。
3) isocyanatopropy litriethoxy silane
异氰酸酯基甲基三乙氧基硅烷
1.
siloxane-modified polyester was synthesized with isocyanatopropy litriethoxy silane and saturated polyester resin AK3010, under the reaction between the hydroxyl and the socyanate-group, and characterized by the test of FTIR, TG, DSC.
本文利用异氰酸酯基甲基三乙氧基硅烷中的-NCO，与饱和聚酯树脂AK3010中的游离-OH反应，形成-NHCOO-键的同时将三乙氧基硅基引入饱和聚酯树脂中，制备了几种[OH]／[NCO]不同反应比例的有机硅改性聚酯。
4) γ-(trimethoxysilyl) propyl methacrylate
γ-甲基丙烯酸丙酯基三甲氧基硅烷
5) γ-aminopropyltriethoxysilane
γ-氨丙基三乙氧基硅烷
1.
With zirconium oxychloride and γ-aminopropyltriethoxysilane(KH-550) as precursor, the hybrid film composed of zirconia and organosilicone was prepared on polycarbonate through co-condensation reactions by sol-gel method.
以氧氯化锆(ZrOCl_2·8H_2O)和γ-氨丙基三乙氧基硅烷(KH-550)为先驱体,采用溶胶-凝胶法通过共缩聚反应在聚碳酸酯(PC)板表面制备了锆/有机硅复合薄膜,采用TG/DTA、FTIR、UV-VIS、金相显微镜及铅笔硬度测试方法对复合薄膜的结构及性能进行表征。
6) γ-chloropropyltriethoxysilane
γ-氯丙基三乙氧基硅烷
1.
Analysis of Impurities in Commercial γ-chloropropyltriethoxysilane by GC-ITD;
γ-氯丙基三乙氧基硅烷及其杂质的GC-ITD分析
补充资料：异氰酸十八烷醇酯
分子式：C19H37NO
分子量：299.51
CAS号：112-96-9
性质：在常温下为无色略带混浊的液体，易燃。熔点21℃，沸点170℃（266.7Pa），相对密度0.8625，闪点184℃（开杯）。
制备方法：由十八胺在氯苯溶剂中与光气反应生成十八烷基胺酰氯，然后加热分解、减压精馏而得。原料消耗定额：十八胺1200kg/t、光气1170kg/t、氯苯260kg/t。
用途：主要用作印染助剂、毛纺织品柔软剂VS的合成原料，也可用于防水织物表面处理。
分子量：299.51
CAS号：112-96-9
性质：在常温下为无色略带混浊的液体，易燃。熔点21℃，沸点170℃（266.7Pa），相对密度0.8625，闪点184℃（开杯）。
制备方法：由十八胺在氯苯溶剂中与光气反应生成十八烷基胺酰氯，然后加热分解、减压精馏而得。原料消耗定额：十八胺1200kg/t、光气1170kg/t、氯苯260kg/t。
用途：主要用作印染助剂、毛纺织品柔软剂VS的合成原料，也可用于防水织物表面处理。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。