1) refractory product
耐材制品
2) refractory
耐材
1.
As the rpsults the purpose of reducing the patching refractory consumption is thus achieved.
从改进冶炼操作工艺及优化溅渣护炉工艺提高溅渣护炉效果两方面入手, 降低了钢水对炉衬(包括溅渣层)的侵蚀, 提高补炉层(包括溅渣层)的抗侵蚀能力, 实现了降低补炉耐材的目的, 取得了明显的效果。
3) Magnesian refractory
Mg质耐材
4) refractory consumption
耐材消耗
1.
In order to increase life of tundish and continuous heats, reduce refractory consumption, measures such as improving tundish lining work, using dry vibratory pressing tundish, setting up baffle wall, improving deoxidization process, increasing EAF productivity, redesigning seal structure of mould, adopting tundish rejointing technology etc.
为了提高中间包使用寿命和连拉炉数、降低耐材消耗,莱钢特钢厂采取了改进中间包砌筑工艺、应用干法振动成型式中间包、应用导流隔墙、改进LF脱氧工艺、提高电炉生产率、改进结晶器密封结构、应用中间包重接技术等多项措施,使吨钢耐材消耗降低7 57元,单包连拉炉数达到35炉。
2.
According to the actually operating conditions in steel-making plant of Pansteel,the major reasons adout the refractory consumption in 2006 have been analysed, the means about reducing refractory in 2007 have been bringed forward.
结合攀钢转炉炼钢工艺操作情况,分析了06年转炉耐材消耗增加的主要原因,提出了07年降低攀钢转炉耐材消耗的具体措施,07年攀钢转炉耐材消耗降低明显。
5) low carbon refractory
低碳耐材
6) firebrick material
耐材材质
参考词条
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。