1) caustic embrittlement
碱脆
1.
In this paper, the causes about the caustic embrittlement occurred in the pipelines of the sodium hydroxide system in the company and main preventive measures for it were introduced.
介绍我公司烧碱管线系统碱脆产生的原因及主要预防措施。
2.
According to caustic embrittlement phenomenon existed in test run of 1 100 m 2 natural circulation evaporator proper construction scheme is determined which contain raw materials selection, welding quality improvement, stress elimination and other measures.
针对 110 0m2 自然循环蒸发器在试生产过程中的碱脆现象 ,结合蒸发器大修 ,提出合理选用材质、提高焊接质量、采用清除应力退火等措施的施工方案 ,经过近三年的实践证明 ,碱脆现象基本得到控制和消
2) caustic brittleness
碱性脆化;碱脆性
3) caustic embrittlement cracking
碱脆开裂
1.
The high Mn steel caustic embrittlement cracking was distinct in corrosion.
结果表明,高锰钢的平均腐蚀速率显著高于中碳铬合金钢,腐蚀过程中高锰钢有较严重的碱脆开裂现象。
4) caustic SCC at high temperature
高温碱脆
5) caustic embrittlement
碱蚀致脆
6) alkali embrittlement
碱脆性
补充资料：碱脆
分子式：
CAS号：
性质： 钢铁材料在碱溶液中的应力腐蚀破裂。碳钢的碱脆一般发生在碱浓度大于5％、温度超过50℃的环境中。随碱浓度和温度升高，破裂敏感性增大，主要发生在锅炉和制碱设备中。不锈钢的碱脆一般发生在沸点以上温度，但在50％NaOH中沸点以下也可能破裂。
CAS号：
性质： 钢铁材料在碱溶液中的应力腐蚀破裂。碳钢的碱脆一般发生在碱浓度大于5％、温度超过50℃的环境中。随碱浓度和温度升高，破裂敏感性增大，主要发生在锅炉和制碱设备中。不锈钢的碱脆一般发生在沸点以上温度，但在50％NaOH中沸点以下也可能破裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。