1) coupling-chelating agent
偶联螯合剂
1.
The results show that:based on selecting proper molar ratio(F/U≤13),changing synthetic technology,adding coupling-chelating agent(10%) and so on,low toxicity UF resins with good comprehensive performances could be made.
在低物质的量比条件下,分析讨论了脲醛胶的各项力学性能,甲醛释放机理,通过研究表明:选择适合的物质的量比(F/U≤1 3)、改进合成工艺、添加偶联螯合剂(1 0%)等,可生产出综合性能较好的低毒脲醛胶,胶合板甲醛释发量达到E1级(≤1 5mg/L),力学性能符合GB/T9846-1988及GB/T15104-1994标准要求。
2) Wt-200S
螯合磷酸酯钛偶联剂
1.
Rare earth coupling agent and Wt-200S were chosen as compound modifier for magnesium hydroxide by wet-modification method.
选择稀土偶联剂/螯合磷酸酯钛偶联剂作为氢氧化镁的复合改性剂,采用湿法改性处理氢氧化镁。
3) composite coupling agent
复合偶联剂
1.
A new interfacial reinforcing agent is introduced in the composite material of calcium carbonate/polyethylene,and it compounds with coupling agent to form a composite coupling agent,which can greatly reinforce the interfacial combination strength between calcium carbonate and polyethylene,and then greatly improve the impact strength of casting plastic products.
在碳酸钙-聚乙烯复合材料的界面之间,引入了一种新型的界面增强剂与偶联剂复合,大大提高了碳酸钙与聚烯烃的界面结合强度,从而大幅度提高注塑产品的冲击强度;考察了复合偶联剂的配比及其含量、碳酸钙的含量对复合材料性能的影响。
4) polymerization-coupling reactant
聚合偶联剂
5) chelation crosslinking
螯合交联
1.
In corporation of crosslinking agent zinc acetate will lead the chelation crosslinking between carboxylicion and metalion.
通过加入金属盐交联剂醋酸锌,使羧基离子与金属离子键合形成螯合交联,研究了羧基含量与加入醋酸锌后不同的n(Zn2+)∶n(—COOH)对乳液性能的影响,自交联乳液制得的涂膜铅笔硬度达到2H,耐水性达96 h以上。
6) chelating agent
螯合剂，螯和剂
补充资料：偶氮化合物类高分子螯合剂
分子式：
CAS号：
性质：氮配位原子以偶氮形式（R—N=N—R′）存在的高分子螯合剂。一般可以通过聚苯乙烯树脂的偶氮化反应引入偶氮结构。这种螯合树脂在盐酸溶液中可以吸附Cu2+，La3+，ZrO2+等离子，一般多用于稀土元素的浓缩和富集。以聚对氯甲基苯乙烯为原料或含有氨基的偶氮化合物反应也可以得到含有偶氮基团的高分子螯合剂。它们对Cu2+和La3+具有选择性吸附能力。偶氮型高分子螯合物多具有特征颜色。
CAS号：
性质：氮配位原子以偶氮形式（R—N=N—R′）存在的高分子螯合剂。一般可以通过聚苯乙烯树脂的偶氮化反应引入偶氮结构。这种螯合树脂在盐酸溶液中可以吸附Cu2+，La3+，ZrO2+等离子，一般多用于稀土元素的浓缩和富集。以聚对氯甲基苯乙烯为原料或含有氨基的偶氮化合物反应也可以得到含有偶氮基团的高分子螯合剂。它们对Cu2+和La3+具有选择性吸附能力。偶氮型高分子螯合物多具有特征颜色。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。