1) inorganic whisker
无机盐晶须
2) Inorganic whiskers
无机晶须
3) Inorganic whisker material
无机晶须材料
1.
Inorganic whisker material is divided into 3 classifications: high-temperature whisker, mid-temperature whisker and low-temperature whisker accoding to the difference temperature of the used whisker.
无机晶须材料从使用温度条件来讲可分为三类:高温晶须、中温晶须和低温晶须;我们把每类晶须选择较为典型的几种做了较为详尽的介绍:一般性质、制备方法及复合材料等。
4) Magnesium salt whisker
镁盐晶须
1.
Study on properties of composites of PP and magnesium salt whisker;
PP镁盐晶须复合材料的性能研究
2.
Study and application of magnesium salt whisker enhanced material;
镁盐晶须增强材料的研究及应用
3.
The results show that: the optimum proportion of EVA: LDPE is 6:4(by weight);adding magnesium salt whisker enhances the tensile strength and elongation at break,and the magnesium salt whisker cooperates with ATH to improve the decomposition temperature of the composites,so that it enhances Limited .
通过拉伸性能、燃烧性能测试及热失重-差示扫描量热分析(TG-DSC),研究了EVA、镁盐晶须和相容剂的用量对LDPE/EVA/ATH复合体系的影响。
5) magnesium hydroxide sulfate whisker
镁盐晶须
1.
Foam composites of phenolic/magnesium hydroxide sulfate whisker were prepared via in-situ polymerization.
采用原位复合方法制备了镁盐晶须/酚醛泡沫复合材料,研究了镁盐晶须对泡沫粉化程度、回弹性以及力学性能的影响,并通过热失重和氧指数分析了镁盐晶须/酚醛泡沫复合材料的热稳定性和阻燃性。
2.
A new kind of automobile brake composites reinforced by magnesium hydroxide sulfate whisker (M-HOS) and prepared by molding compression has been developed.
针对我国传统汽车制动材料在应用过程中存在的摩擦热衰退问题,采用模压成形工艺,利用无机镁盐晶须增强酚醛树脂研制一种新型汽车制动复合材料。
6) borate whiskers
硼酸盐晶须
1.
Study on property of epoxy resin reinforced With borate whiskers;
硼酸盐晶须改性环氧树脂性能研究
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。