1) metallic ceramic nanocomposite
金属陶瓷纳米复合材料
2) nanometer cermet
纳米金属陶瓷材料
1.
The technology and property of nanometer cermet is studied with new microwave sintering technology.
采用微波烧结新技术研究了纳米金属陶瓷材料的烧结工艺与性能。
3) ceramic nanocomposite
纳米复合陶瓷材料
1.
Al2O3/(W,Ti)C ceramic nanocomposites were fabricated from nanocrystalline α-Al2O3,micro-crystalline α-Al2O3 and (W,Ti) C.
采用纳米和亚微米级的α-Al2O3,以及微米级的(W,Ti)C粉体为原料,制备了Al2O3/(W,Ti)C纳米复合陶瓷材料。
2.
Al2O3/(W,Ti)C ceramic nanocomposites were fabricated by hot pressing technique from nanocrystalline α-Al2O3,micro-crystalline α-Al2O3 and(W,Ti)C.
使用纳米、亚微米级的α-Al2O3粉体和微米级的(W,Ti)C粉体为原料,采用热压烧结工艺制备了Al2O3/(W,Ti)C纳米复合陶瓷材料。
4) ceramic nanocomposite
纳米陶瓷复合材料
1.
Al 2O 3/SiC ceramic nanocomposites were fabricated from nanocrystalline α Al 2O 3 (10?nm in diameter) and SiC (15?nm in diameter) powders.
采用一次粒径分别为 10nm和 15nm的α Al2 O3 和SiC粉体为原料 ,制备了Al2 O3 /SiC纳米陶瓷复合材料·纳米SiC颗粒明显抑制Al2 O3 基体晶粒的长大 ,SiC体积分数超过 4 %时 ,材料的断裂方式由沿晶断裂变为穿晶断裂·随SiC含量的增加 ,Al2 O3 /SiC纳米复合材料的硬度增大·材料的弯曲强度和断裂韧性在SiC体积分数为 5 %时达到最大值·最大三点弯曲强度和断裂韧性分别为 6 4 1MPa和 4 7MPam1/2 ,明显高于热压单相Al2 O3 陶瓷 (344MPa和 3 1MPam1/2 ) ·复合材料的强化主要来源于内晶颗粒残余应力强化和晶粒细化强
6) ceramic nanocomposites
陶瓷纳米复合材料
补充资料：梯度金属/陶瓷基复合材料
梯度金属/陶瓷基复合材料
metal/eeramiematrix gradieflt eomPosites
梯度金属/陶瓷基复合材料metal/ceramicmatrix gradient eomposites金属组分与陶瓷组分逐渐梯变而形成的复合材料。属梯度功能材料。其一侧是高硬度、高强度并具有很好的耐高温性能的陶瓷层;另一侧是容易加工和焊接的金属;中间部位有一组分逐渐过渡的区域和过渡层。这种过渡层的存在可以大大缓和金属与陶瓷之间的热应力，从而解决金属与陶瓷的难接合问题。 目前研究比较多的材料组成有PSZ/W、M四/SUS3O4、TIB/Cu、Si3N‘/合金、SIC/合金等。这些材料制备的难点在于，陶瓷材料需要1500℃以上温度的烧结工艺才能致密化，而一般金属材料难于在如此高温下与陶瓷稳定共存，或是在高温下剧烈反应生成脆性合金相，或是相容性差而相互分离。为此，除粉末冶金法外，逐段加热烧结法、金属压渗法、自蔓燃合成法(S HS)等新的复合工艺和烧结工艺，得到越来越多的应用。(李建保)