3) zinc-base aluminum alloy
锌基铝合金
4) high aluminum Zn-based alloys
高铝锌基合金
1.
As a new kind of alloy, high Aluminum Zn-based alloys have found wide use in wear-resisting machinery in recent years.
高铝锌基合金是近年来在耐磨行业应用日益广泛的一类新型合金。
5) zinc/aluminium based corrosion resistance coating
锌铝基耐蚀涂层
1.
To solve the performance problems, low hardness and poor wear resistance and antifriction, of the zinc/aluminium based corrosion resistance coating at the special high speed and large friction service conditions, a trial adding diamond particles into the coating was made to enhance the coating properties.
为解决锌铝基耐蚀涂层在高速、强摩擦等特殊服役条件下硬度低、耐磨减摩性能差等问题,尝试通过添加金刚石粒子对其进行强化。
2.
To solve the used problem of the Zinc/Aluminium based corrosion resistance coating under the special high speed and large friction service conditions, a trial adding SiC nanoparticles into the coating was made to increase the coating hardness and strength.
为解决锌铝基耐蚀涂层在高速、强摩擦等特殊服役条件下的使用问题,探索性地添加SiC纳米粒子对锌铝基耐蚀涂层进行改性,以提高涂层的硬度和强度。
6) High aluminum zinc based alloy
高铝锌基合金
1.
The high aluminum zinc based alloy ZA27 is a good substitute material for highstrength anti-friction copper alloys and aluminum alloys.
高铝锌基合金是铜合金和铝合金等高强度磨损件的理想替代材料，虽然人们已经就其耐磨性能进行了一些研究，但对这种合金更全面的摩擦学性能研究，尤其是有关它的磨损机理之研究却还是一个尚未深入开展的课题。
补充资料：铝-锌系铸造铝合金
分子式：
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。