1) Refining Slag Series Containing BaO
含BaO精炼渣系
2) BaO contained slag series
含BaO渣系
1.
The results showed that under the condition of adding 8 kg/t of BaO contained slag series desulphurizing agent, the average desulphurizing rate ηS≥35%, which compared with that of CaO-based desulphurizing agent without BaO, was relatively improved by 40%; the sulfur capacity(CS′) and sulfur distribution coefficient(Ls) of BaO slag series and mass transf.
结果表明,在含BaO渣系脱硫剂加入量8kg/t的条件下,平均脱硫率ηS≥35%,与不含BaO的CaO基脱硫剂相比,ηS相对提高40%左右。
3) refining slag
精炼渣系
1.
Factors related to increase ot Al content such as refining slag compositions,molten steel composition LF refining time etc.
通过理论计算和工业生产实践研究了不同的渣系、钢水成分、处理时间等对LF精炼过程增铝的影响,不同精炼渣系下钢中夹杂的组成,结果表明采用CaO-SiO2渣系LF处理过程几乎不发生增铝现象,而采用CaO-Al2O3渣系随着处理时间的延长以及钢种成分的区别,钢中铝有不同程度的增加,生产实践结果与理论计算趋势基本一致。
2.
The desulfurization effect for both CaO-Al2O3-MgO-SiO2 and CaO-Al2O3-MgO-SiO2-CaF2 refining slag are studied in ladle furnace process.
在钢包精炼炉上对CaO-Al2O3-MgO-SiO2和CaO-Al2O3-MgO-SiO2-CaF2两种精炼渣系的脱硫效果进行了研究。
4) BaO-CaO slag system
BaO-CaO渣系
5) BaO-based slag
BaO基渣系
1.
The slag composition dependence of the dephosphorizing properties of BaO-based slags were studied by chemical equilibrium of phosphorus between slag and stainless liquid steel at 1 773K.
在1773K,通过磷在BaO基渣系和不锈钢粗钢液之间的平衡实验,研究得出了磷酸盐容量和渣组成、光学碱度及温度的关系。
6) BaO Slag Series
BaO系渣
补充资料：含钽锡渣
锡石中以类质同相状态存在的钽、铌，用选矿的方法不能将其分离,在炼锡时进入炉渣,成为含钽锡渣。随着钽矿石的贫化和日趋短缺，锡渣中的钽逐渐成了世界钽的主要来源。20世纪50年代时，它在世界总产钽量中的比重微不足道，60年代末达到25％，70年代末已超过50％。从中国南部经泰国和马来西亚的锡矿带钽含量最富。中国广西、广东、云南、湖南、江西等省均有含钽锡矿和含钽锡渣。
各国锡渣的钽含量不等,典型的扎伊尔锡渣含Ta2O5为12％,泰国为8％，马来西亚为3～4％。其他一般锡渣中含Ta2O5小于2％。锡渣富集成含(Ta+Nb)2O5大于30％的人造钽精矿，再采用火法和湿法冶炼。火法一般是将锡渣和焦炭（或铝粒）、石灰混合，在电弧炉中还原熔炼，生成铁钨锡钽铌合金,然后将合金用电解法、NaNO3氧化焙烧法和酸碱处理。湿法只有氟氢酸－氟硅酸工艺取得了好的经济效果。
各国锡渣的钽含量不等,典型的扎伊尔锡渣含Ta2O5为12％,泰国为8％，马来西亚为3～4％。其他一般锡渣中含Ta2O5小于2％。锡渣富集成含(Ta+Nb)2O5大于30％的人造钽精矿，再采用火法和湿法冶炼。火法一般是将锡渣和焦炭（或铝粒）、石灰混合，在电弧炉中还原熔炼，生成铁钨锡钽铌合金,然后将合金用电解法、NaNO3氧化焙烧法和酸碱处理。湿法只有氟氢酸－氟硅酸工艺取得了好的经济效果。