1) inverse titrating chemical co-precipitation
反滴定化学共沉淀
1.
MgFe_2O_4 composite oxide nano-powder of spinel-type was prepared by inverse titrating chemical co-precipitation method, and its microstructure was characterized by means of powder XRD and TEM.
用反滴定化学共沉淀法制备了纳米尺寸尖晶石型的复合金属氧化物MgFe_2O_4粉体。
2) reverse-titration co-precipitation
反向滴定共沉淀法
1.
40) as the cathode materials for intermediate temperature solid oxide fuel cell were prepared by reverse-titration co-precipitation method with metal-nitrates as starting materials and mixed alkali (NaOH and Na2CO3) as a precipitating agent.
5范围内,反向滴定共沉淀法得到的前驱体在800℃煅烧4h可以合成出纯度高、组份均匀的单一钙钛矿相的LSCCF粉料。
3) reverse-coprecipitation
反向化学共沉淀
1.
The PrxCe1-xO2-δ nano oxides were synthesized by the reverse-coprecipitation method, loaded on MWCNT.
通过反向化学共沉淀法制备了PrxCe1-xO2-δ稀土纳米复合氧化物作为助催化掺杂剂,将其包覆在多壁碳纳米管(MWCNTs)的表面作为催化剂复合载体,然后使用了柠檬酸盐-KBH4液相还原法制备了粒径分布均匀、性质稳定的Pt纳米溶胶,并沉积在上述载体中得到负载型Pt-PrxCe1-xO2-δ/CNT复合电催化剂,制备的催化剂中Pt载量为20%(质量分数)。
4) reverse-titration precipitation method
反向滴定沉淀法
5) chemical co-precipitation
化学共沉淀
1.
Study of La-doped nanosized SnO_2 by chemical co-precipitation;
化学共沉淀法制备镧掺杂纳米二氧化锡的研究
2.
W-Ni-Fe composite oxides nano-powder has been prepared from finely grained tungstate synthesized by chemical co-precipitation and oxided at 600℃.
以化学共沉淀法制备的盐在600℃下氧化,可得W-Ni-Fe复合氧化物,检测分析显示W-Ni-Fe复合氧化物粉的晶粒直径XRD-d为36 nm,W-Ni-Fe复合氧化物粉的颗粒粒径BET-d为98 nm;从SEM图分析看出该复合氧化物粉颗粒团聚性低,压坯EDXS的表面电子图像和元素面分布图显示该复合氧化物粉中W、Ni、Fe元素分布状态是高度均匀分布。
3.
In this work,nanometer magnetite(Fe_3O_4) particles were prepared by chemical co-precipitation,NH_3·H_2O was chosen as precipitating agent,and was added to the mixed aqueous solution containing ferric and ferrous ions to produce nanometer Fe_3O_4 particles.
采用化学共沉淀法制备纳米磁性Fe3O4粒子。
6) chemical coprecipitation
化学共沉淀
1.
Antimony-doped tin oxide (ATO) nanorods with rutile structure were successfully prepared by annealing nanoscale precursor powders at 1 000～1 100(°C) for 1～3 h, which were produced by chemical coprecipitation using SnCl_4·5H_2O and SbCl_3.
以SnCl4·5H2O和SbCl3为原料,采用化学共沉淀法制得纳米级掺锑二氧化锡(ATO)的前驱物,经1000～1100°C焙烧1～3h,成功制备了直径为10～40nm,长为60～500nm的金红石结构的ATO纳米棒。
2.
A series of (Sr1-xPbx) TiO3 ceramic powders were prepared through chemical coprecipitation process.
采用化学共沉淀法制备了一系列(Sr1-xPbx)TiO3陶瓷粉体,通过差热-热重(DTA-TG)分析确定了共沉淀产物的煅烧温度。
3.
71μm to prepare the W-Cu composite by using chemical coprecipitation.
以H2WO4和CuSO4·H2O(W:Cu=70g:30g)为原料,采用化学共沉淀方法制备W-Cu化合物粉末,其反应条件为:反应温度25℃±1℃,pH值5。
补充资料：化学共沉淀法制粉
化学共沉淀法制粉
preparation of powder by chemical coprecipitation method
化学共沉淀法制粉preparation of powder byehemieal eopreeipitation method用一种或多种金属盐溶液，通过化学反应形成沉淀物，然后经过脱除溶剂和加热分解而制得陶瓷粉体的方法。由这种方法制得的粉体均匀性好，其中所包含的正离子能在原子大小水平上混合在一起，反应性能好，易于烧结。 化学共沉淀制粉的工艺原理是:将沉淀剂加入溶液中，发生下列反应 A++B-一 AB土当溶液中A十与B一离子浓度的乘积〔A十〕·〔B一〕大于其溶度积S协B时，溶液即呈过饱和而AB化合物发生沉淀。在实际反应中，沉淀过程是很复杂的，常常需要调节溶液的酸度、反应温度、沉淀剂的浓度及其加入速度等来扛制沉淀反应速度和沉淀是否完全。当溶液中存在有多种能与沉淀剂发生反应的离子时，生成物中溶度积最小的化合物首先产生沉淀，随着沉淀剂的继续加入和浓度的增加，较大溶度积的化合物会依次被沉淀下来。为使沉淀反应完全，往往使用过量的沉淀剂，以增大离子的浓度乘积。这样在阳离子的种类、大小相似时，就更易于产生共晶物质而共同沉淀出来。这种方法对在某些基体中掺入微量活性离子尤为方便。 化学共沉淀方法可分为:①直接用过量沉淀剂使络液中全部阳离子同时沉淀下来成为混合物;②通过特定沉淀剂，使阳离子形成符合化学计量比要求的前驱体化合物。例如BaTIO(CZO4):·4 HZO(Ba与 Ti比为1:1)沉淀即属此情况;③为避免沉淀剂局部过浓，沉淀剂可通过化学反应在溶液中逐步生成，从而产生均相沉淀。例如把尿素溶解到反应液中，通过加热到70℃以上，使尿素水解产生氨CO(NHZ)2+3 HZO垫2 NH。·HZO+COZ氨在溶液内一旦生成，即与金属离子反应生成沉淀，这样发生的氮浓度低、均匀，获得的粉体纯度高，粒径大小和形状均齐性好。 共沉淀法的适用范围广，除可用于制备各种难溶的金属氢氧化物和氧化物外，还可用于制备碳酸盐、草酸盐、硫酸盐和磷酸盐等。但是如果两种反应物在水中溶解度相差过大，或反应物不是以相同的速度沉淀时，或生成物形成稳定的过饱和溶液时，化学共沉淀法即不宜使用。(袁启华)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条