In order to recovering remained vanadium from high vanadium ferrovanadium bearing high A12O3 with electric -silicothermic process, transforming slag conposition with adjusting material in furnace charge can recover vanadium economically and can produce self-willed ferrovanadium bearing high silicon and low vanadiu

利用电硅热法提取含高Al_2O_3成分的高钒铁炉渣中残钒,在炉料中配入调渣物料改造渣型后,能较经济地提取出钒元素,生产自用高硅低钒铁。

The processes of smelting high vanadium ferrovanadium with vanadium pentoxide and vanadium trioxide are probed into, appropriate parameters are pointed out, and the two processes of smelting high vanadium ferrovanadium are compared.

对使用五氧化二钒和三氧化二钒混合料冶炼高钒铁的工艺进行了探讨,指出了适宜的工艺参数,并对生产高钒铁的两种工艺技术进行了比较。

2) high V-Cr white cast iron 点击朗读

高钒-铬白口铸铁

3) high vanadium electrode 点击朗读

高钒铸铁焊条

The influence of RE on high vanadium electrode was studied by comparative tests. 点击朗读

通过药皮含稀土焊条与普通焊条的对比试验 ,研究了稀土对高钒铸铁焊条的性能的影响。

更多例句>>

4) Fe-V-C alloy 点击朗读

高钒铁碳合金

5) ferrovanadium [,ferəvə'neidiəm] 点击朗读

钒铁

The mainly preparation of ferrovanadium is aluminothermic reduction currently. 点击朗读

钒铁是生产工具钢、耐热钢的一种重要中间合金,目前主要采用铝热法生产。

An ICP AES method for the determination of Cu,Si,Al,P,Cr,Ni,Mn,W in ferrovanadium has been established, based on the selection of proper wavelength and background correction.

叙述采用等离子发射光谱法同时测定钒铁中的铜、硅、铝、磷、铬、镍、钨、锰等微量元素 ,试样用稀王水分解 ,选择适当的波长与背景校正进行分析测定 ,方法回收率在 95%～ 1 0 5%之间 ,相对标准偏差均小于 4% ,本方法快速准确 ,精密度良好。

To promote development of low alloy steel bearing vanadium and mitrogen,the process,conditions and products of preparing nitrided ferrovanadium and vanadium nitride are introduced on the basis of main documents.

为推动含钒氮低合金钢的发展 ,在查阅主要文献的基础上 ,重点介绍了氮化钒铁及氮化钒制备的工艺方法、条件及产品情况。

更多例句>>

6) FeV

钒铁

TRIAL PRODUCTION OF HRB400 BAR BY MICROALLOYING PROCESS OF "FeV+NITROGEN ENRICHMENT AGENT";

“钒铁+富氮剂”微合金化HRB400钢筋生产试验

更多例句>>

补充资料：钒铁精矿直接提钒

钒铁精矿直接提钒
direct extraction of vanadium from ferro-vanadium concentrate

fantie!ingkuang zhi」ie tifan钒铁精矿直接提钒(direet extraetion of van.adium from ferro一vanadium eoneentrate)钒铁精矿钠盐焙烧制取五氧化二饥的机提取方法。又称铁精矿水法提饥。饥钦磁铁精矿经磨矿、磁选所得食钒铁精矿通常含v20。0.5%~2%和全铁50%一“%，可不经高炉炼铁和铁水吹钒渣而直接进行钠引焙烧和水浸出提饥，提饥后的铁精矿再用作炼铁原料原理经细磨的钒铁精矿和钠化剂(碱、芒硝或员明粉N助50‘)制成粒或造成球，在焙烧炉内进行氧仁钠化焙烧，钒铁精矿中的钒便被氧化生成V205: ，_~，，~、5~_一。。、，~ 2(Feo·VZO:)十份O:一Fe:03+2V2O5 “、‘’~’‘一J’2一‘一‘一‘’一‘一‘V20。再和NaZso.分解产生的Na20作用，生成水译性NaVO:: __v针~_，_.--一.5一 SNaZSO‘一SNaZO十5502十.份02 ~’一‘~~吸~’一‘一’-一一‘’2一“ 2V2O5+ZNa:O一4NaVOa ，___，~、.5~一~.。，，~ 2(FeO’VZO，)+to，一Fe，03+”V，O”总反应为: 2(FeO·V20，)+SNaZSO-一4NaV03+3NaZO+Fe:03+5502 用水浸出焙烧产物过程中，NaVO:进入溶液与大部分不溶产物分离，然后再从经净化处理过的含钒溶液中沉淀出钒的化合物。工艺根据钠化焙烧所用的主体设备，钒铁精矿直接提饥又分为竖炉钠化焙烧、流态化床钠化焙烧、回转窑钠化烙烧和链算机回转窑钠化焙烧四种方法。竖炉钠化焙烧提钒芬兰劳塔鲁基(Rautaruuk-ki)钢铁公司所属的奥坦梅基(Otan俪ki)饥厂和木斯特瓦拉(Mustavaara)饥厂均采用钒铁精矿加钠盐造球，竖炉钠化烙烧的提钒方法.奥坦梅墓饥厂所用的原料成分(质量分数。/%)为:全Fe6s.4，TioZs.2，vZos1 .125，5102 0.4，Cao 0.06，Mg00·24，Ai203o·5。饥铁精矿磨至一。.o38mm粒级占85%，加入占料量2.2%~2.3%的芒硝(NaZSO;)或1.6%~1.8%NaZC03，用混料圆筒(直径 2.7m，长gm，倾角70)造球机制成直径13~16mm的球粒，入直径3~3.3m、高15m圆形竖炉中进行钠化烙烧。烙烧产物在20个浸出峨中浸出。浸出嫩用钢板焊成，外部保温，雄径2.sm、高12.sm、容积6om3，可装钠化球sot。浸出后的钠化球送高炉炼铁。浸出液含钒20~259/L，在6个10m，沉淀嫩中加硫酸和硫酸按在363K温度下沉淀出vZOS。沉饥后尾液含饥。.089/L，经进一步处理后排放.竖炉作业率90%，热耗为每吨球团18~20L重油，蒸汽消耗为每吨vZo。600L，电耗为每吨V20。3300kw·h，产品五氧化二钒纯度为”.5%，钒收率78写。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

钒钛铁矿铁和钒钒钛铸铁

铁钒高钒钒铁微粒钒钛生铁锆钒铁钒钛铁水

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 高钒铁 1) high vanadium ferrovanadium 高钒铁 1. In order to recovering remained vanadium from high vanadium ferrovanadium bearing high A12O3 with electric -silicothermic process, transforming slag conposition with adjusting material in furnace charge can recover vanadium economically and can produce self-willed ferrovanadium bearing high silicon and low vanadiu 利用电硅热法提取含高Al_2O_3成分的高钒铁炉渣中残钒,在炉料中配入调渣物料改造渣型后,能较经济地提取出钒元素,生产自用高硅低钒铁。 2. The processes of smelting high vanadium ferrovanadium with vanadium pentoxide and vanadium trioxide are probed into, appropriate parameters are pointed out, and the two processes of smelting high vanadium ferrovanadium are compared. 对使用五氧化二钒和三氧化二钒混合料冶炼高钒铁的工艺进行了探讨,指出了适宜的工艺参数,并对生产高钒铁的两种工艺技术进行了比较。 2) high V-Cr white cast iron 高钒-铬白口铸铁 3) high vanadium electrode 高钒铸铁焊条 1. The influence of RE on high vanadium electrode was studied by comparative tests. 通过药皮含稀土焊条与普通焊条的对比试验 ,研究了稀土对高钒铸铁焊条的性能的影响。更多例句>> 4) Fe-V-C alloy 高钒铁碳合金 5) ferrovanadium [,ferəvə'neidiəm] 钒铁 1. The mainly preparation of ferrovanadium is aluminothermic reduction currently. 钒铁是生产工具钢、耐热钢的一种重要中间合金,目前主要采用铝热法生产。 2. An ICP AES method for the determination of Cu,Si,Al,P,Cr,Ni,Mn,W in ferrovanadium has been established, based on the selection of proper wavelength and background correction. 叙述采用等离子发射光谱法同时测定钒铁中的铜、硅、铝、磷、铬、镍、钨、锰等微量元素 ,试样用稀王水分解 ,选择适当的波长与背景校正进行分析测定 ,方法回收率在 95%～ 1 0 5%之间 ,相对标准偏差均小于 4% ,本方法快速准确 ,精密度良好。 3. To promote development of low alloy steel bearing vanadium and mitrogen,the process,conditions and products of preparing nitrided ferrovanadium and vanadium nitride are introduced on the basis of main documents. 为推动含钒氮低合金钢的发展 ,在查阅主要文献的基础上 ,重点介绍了氮化钒铁及氮化钒制备的工艺方法、条件及产品情况。更多例句>> 6) FeV 钒铁 1. TRIAL PRODUCTION OF HRB400 BAR BY MICROALLOYING PROCESS OF "FeV+NITROGEN ENRICHMENT AGENT"; “钒铁+富氮剂”微合金化HRB400钢筋生产试验更多例句>> 补充资料：钒铁精矿直接提钒钒铁精矿直接提钒 direct extraction of vanadium from ferro-vanadium concentrate fantie!ingkuang zhi」ie tifan钒铁精矿直接提钒(direet extraetion of van.adium from ferro一vanadium eoneentrate)钒铁精矿钠盐焙烧制取五氧化二饥的机提取方法。又称铁精矿水法提饥。饥钦磁铁精矿经磨矿、磁选所得食钒铁精矿通常含v20。0.5%~2%和全铁50%一“%，可不经高炉炼铁和铁水吹钒渣而直接进行钠引焙烧和水浸出提饥，提饥后的铁精矿再用作炼铁原料原理经细磨的钒铁精矿和钠化剂(碱、芒硝或员明粉N助50‘)制成粒或造成球，在焙烧炉内进行氧仁钠化焙烧，钒铁精矿中的钒便被氧化生成V205: ，_~，，~、5~_一。。、，~ 2(Feo·VZO:)十份O:一Fe:03+2V2O5 “、‘’~’‘一J’2一‘一‘一‘’一‘一‘V20。再和NaZso.分解产生的Na20作用，生成水译性NaVO:: __v针~_，_.--一.5一 SNaZSO‘一SNaZO十5502十.份02 ~’一‘~~吸~’一‘一’-一一‘’2一“ 2V2O5+ZNa:O一4NaVOa ，___，~、.5~一~.。，，~ 2(FeO’VZO，)+to，一Fe，03+”V，O”总反应为: 2(FeO·V20，)+SNaZSO-一4NaV03+3NaZO+Fe:03+5502 用水浸出焙烧产物过程中，NaVO:进入溶液与大部分不溶产物分离，然后再从经净化处理过的含钒溶液中沉淀出钒的化合物。工艺根据钠化焙烧所用的主体设备，钒铁精矿直接提饥又分为竖炉钠化焙烧、流态化床钠化焙烧、回转窑钠化烙烧和链算机回转窑钠化焙烧四种方法。竖炉钠化焙烧提钒芬兰劳塔鲁基(Rautaruuk-ki)钢铁公司所属的奥坦梅基(Otan俪ki)饥厂和木斯特瓦拉(Mustavaara)饥厂均采用钒铁精矿加钠盐造球，竖炉钠化烙烧的提钒方法.奥坦梅墓饥厂所用的原料成分(质量分数。/%)为:全Fe6s.4，TioZs.2，vZos1 .125，5102 0.4，Cao 0.06，Mg00·24，Ai203o·5。饥铁精矿磨至一。.o38mm粒级占85%，加入占料量2.2%~2.3%的芒硝(NaZSO;)或1.6%~1.8%NaZC03，用混料圆筒(直径 2.7m，长gm，倾角70)造球机制成直径13~16mm的球粒，入直径3~3.3m、高15m圆形竖炉中进行钠化烙烧。烙烧产物在20个浸出峨中浸出。浸出嫩用钢板焊成，外部保温，雄径2.sm、高12.sm、容积6om3，可装钠化球sot。浸出后的钠化球送高炉炼铁。浸出液含钒20~259/L，在6个10m，沉淀嫩中加硫酸和硫酸按在363K温度下沉淀出vZOS。沉饥后尾液含饥。.089/L，经进一步处理后排放.竖炉作业率90%，热耗为每吨球团18~20L重油，蒸汽消耗为每吨vZo。600L，电耗为每吨V20。3300kw·h，产品五氧化二钒纯度为”.5%，钒收率78写。说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条钒钛铁矿铁和钒钒钛铸铁

©2011 dictall.com