1) low-pressure injection
低压灌注成形
2) low-pressure perfusion molding process
低压灌注成型
1.
Based on the principle and the technical characteristics of the low-pressure perfusion molding process that is applied to rapid tooling,this paper developed a mathematic model which reduces the molding process to a 2D and dynamic heat exchange process with an inner heat source.
针对快速模具低压灌注成型的原理和工艺特点,建立了分析成型过程的计算模型,在一定假设成立的条件下将成型过程归结为二维非稳态有内热源的导热过程。
3) low-pressure perfusion molding
低压灌注
1.
Computer simulation for low-pressure perfusion molding;
低压灌注成形的计算机模拟
4) LPIM
低压注射成形
1.
In order to explore a low cost technique which can fabricate complex shape parts efficiently, Low-Pressure Injection Molding (LPIM) combined with Self-propagation High temperature S.
采用低压注射成形制备盲孔细长管毛坯,结合自蔓延高温合成热等静压(SHS-HIP)烧结技术,探索快速、高效合成复杂形状零件的低成本制备工艺。
5) dosage and blending machine
低压灌注设备
1.
This paper introduces the processing procedure of dosage and blending machines and the significance of their proportioning RIM.
介绍低压灌注设备工艺过程及其配比调节的重要性,并以德国E。
6) depression formation
低压形成
1.
Then the depression formation in tropical easterly flow is discussed.
由此讨论了热带东风气流中的低压形成。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。