1) pack aluminization
固体粉末渗铝
2) Low press packing cementation aluminizing
低压固体粉末包埋渗铝
3) pack cementation
粉末渗铝
1.
A CeO_2-modified aluminide coating was obtained after composite electro-deposition Ni and CeO2 panicles on 20 steel with different holding time using pack cementation method.
在粉末渗铝过程中保温不同的时间,获得了CeO_2改性的渗层。
2.
A CeO_2-modified aluminide coating was obtained after composite electro-deposition Ni and CeO_2 particles on 20 steel with different holding time using pack cementation method.
在粉末渗铝过程中保温不同的时间,获得了 CeO_2改性的渗层。
4) solid powder boronisation
固体粉末渗硼
1.
The low speed of solid powder boronisation is the main factor hindering the development of this technique.
固体粉末渗硼的渗速慢是影响该工艺发展的主要问题 。
5) Solid powder
固体粉末
1.
Study on boiling heat transfer enhancement in heat pipe using solid powder;
倾斜热管内加固体粉末强化沸腾换热的研究
2.
Using the fluorescence inspected system and optic fiber,the solid powder fluorescence of oil cuttings is inspected directly.
采用自主搭建的荧光检测系统,利用光纤作为传感组件,对含油岩芯固体粉末样品进行荧光光谱的直接检测,其发射波长、激发波长都得到了可与在溶液中测量相比拟的实验结果。
6) solid aluminizing
固体渗铝
1.
This new solid aluminizing technique can lower the content of the aluminium powder to 10%.
以２∶１的氧化铝加木炭粉为填充剂，１０％铝粉为供铝剂，３％氯化铵为催渗剂，可使铝粉含量降到１０％的新型固体渗铝工艺，不仅能在钢铁表面获得厚而均匀的渗铝层，而且渗剂用后松散性好，试样表面光洁，不存在传统固体渗铝工艺的粘结问题，渗铝件的抗高温氧化性及耐蚀能力远远高于未渗件并可与不锈钢相媲美。
补充资料：热浸渗铝镀层
分子式：
CAS号：
性质：用热浸镀方法在钢表面形成的镀铝层。钢件浸入700～730℃的熔融铝液中，表面生成铝铁化合物，同时一部分铝原子渗入钢铁基体形成扩散层。为使镀层与基体金属牢固结合，一般在热浸后还要进行一次900～980℃的高温处理，使镀层软熔扩散，形成合金层。镀层具有优良的耐大气腐蚀性、抗高温氧化性和抗高温硫腐蚀性能。在石油、化工、能源、海洋工程等领域广泛应用。